Abstract:Hollow titania microparticles about 20-60 mu m in size and hollow titania/carbon composite microparticles about 30-90 mu m in size were prepared by employing commercial Sephadex G-100 beads as the template as well as the carbon precursor. The cross-linked dextran gel template was first immersed in aqueous TiCl4 solution to allow the surface mineralization of titania, resulting in the formation of hollow microparticles of titania/G-100 hybrids. Hollow titania microparticles with a shell thickness adjustable from 1 mu m to 2.5 mu m were fabricated by calcination of the hollow titania/G-100 hybrid microparticles at temperatures from 400 to 700 degrees C in air. On the other hand, hollow titania/carbon composite microparticles similar to 2.6 mu m in shell thickness, which consisted of anatase nanocrystals and amorphous carbon, were obtained by carbonization of the hollow titania/G-100 hybrid microparticles at temperatures from 500 to 700 degrees C in flowing nitrogen. For the titania/carbon composites, the phase transformation from anatase to rutile was suppressed; moreover, the crystallinity of anatase was decreased and the surface area was increased with increasing calcination temperature, in contrast to the case of hollow titania microparticles. The photocatalytic activity of the obtained hollow microparticles of titania and titania/carbon composites was investigated by monitoring the photodegradation of Rhodamine B. In both cases, the product calcined at an intermediate temperature exhibited the highest photocatalytic activity possibly because of a compromise between the anatase crystallinity and the surface area. Compared with the hollow titania microparticles, the hollow titania/carbon composite microparticles exhibit remarkably enhanced photocatalytic activity.

Titania nanotube/hollow sphere hybrid material: Dual-template synthesis and photocatalytic property

Soft-chemical Synthesis of Mesoporous Nitrogen-Modified Titania with Superior Photocatalytic Performance under Visible Light Irradiation

Templated Synthesis of TiO2 Nanotube Macrostructures and Their Photocatalytic Properties

Alkaline hydrothermal synthesis of homogeneous titania microspheres with urchin-like nanoarchitectures for dye effluent treatments.

Hierarchical, Titania-Coated, Carbon Nanofibrous Material Derived from A Natural Cellulosic Substance

Synthesis and Photocatalytic Properties of Hollow Microparticles of Titania and Titania/Carbon Composites Templated by Sephadex G-100

Titania Nanoflowers with High Photocatalytic Activity

Simultaneous formation of silica-protected and N-doped TiO2 hollow spheres using organic–inorganic silica as self-removed templates

Porous Titania/carbon Hybrid Microspheres Templated by in Situ Formed Polystyrene Colloids.

A Dual-Layer Titania Film with Enhanced Photocatalytic Activity

Heterogeneous nanotubular anatase/rutile titania composite derived from natural cellulose substance and its photocatalytic property

Synthesis of TiO2 Hollow Spheres with Tunable Pore Structure and Enhanced Photocatalytic Activity

Titanium Dioxide Nano-Heterostructure with Nanoparticles Decorating Nanowires for High-Performance Photocatalysis

Precise Size Control over Ultrafine Rutile Titania Nanocrystallites in Hierarchical Nanotubular Silica/Titania Hybrids with Efficient Photocatalytic Activity

Efficient fabrication and photocatalytic properties of TiO2 hollow spheres

Tubular Structured Hierarchical Mesoporous Titania Material Derived from Natural Cellulosic Substances and Application As Photocatalyst for Degradation of Methylene Blue

Templated synthesis of titanium dioxide tube-in-tube superstructures with enhanced photocatalytic and lithium storage performances

Bioinspired hierarchical nanotubular titania immobilized with platinum nanoparticles for photocatalytic hydrogen production.

Template Synthesis Of Single-Crystal-Like Porous Srtio3 Nanocube Assemblies And Their Enhanced Photocatalytic Hydrogen Evolution

TiO2-on-C3N4 Double-Shell Microtubes: In-situ Fabricated Heterostructures Toward Enhanced Photocatalytic Hydrogen Evolution.

Hollow Hybrid Titanate/au@tio2 Hierarchical Architecture for Highly Efficient Photocatalytic Application