Deactivation of TiO 2-modified Ag/Al 2O 3 catalyst by SO 2 in the reduction of NO x by propene

Youfa Liu,Jiehong Ooyang,Lishan Wang,Yanxia Su,Junliang Wu,MingLi Fu,Bichun Huang,Daiqi Ye
2012-01-01
Abstract:Ag-base catalysts supported on Al 2O 3 and TiO 2-Al 2O 3 (the mass ratio of TiO 2 to Al 2O 3 was 1 :10) were prepared by sol-get method respectively. The catalysts were characterized by N 2 physisorption, NO x/SO 2-TPD, FT-IR and DRIFTs measurements. The effect of SO 2 on the selective reduction of NO x by propene over the catalysts and the poisoning mechanism were investigated. The results showed that the catalytic activities under the low-medium temperature and the resistance of sulfur poisoning at 400 °C were enhanced after addition of 10% TiO 2.The formation of formate resulted from the introduction of TiO 2 was in favor of the reaction at low temperature, and the competitive adsorption of NO and SO 2 and the formation of silver sulfate were proved to be the main reason for deactivation of 4%Ag/Al 2O 3 catalyst. The addition of TiO 2 could not only improve the adsorption of NO and inhibit the adsorption of SO 2 on catalyst surface, but also inhibit the sulfation of Ag during the catalytic process, which could enhance sulfur poisoning performance of the catalysts eventually.
What problem does this paper attempt to address?