Effect of α-Al 2 O 3 content on microstructures, mechanical properties and purification efficiency on molten steel of MgO-based filters
Ying Liu,Wen Yan,Yu Liu,Qiang Wang,Guangqiang Li,Nan Li
DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.06.041
IF: 5.7
2023-06-18
Journal of the European Ceramic Society
Abstract:In this study, five sets of MgO-based ceramic filters were prepared using porous MgO powder and α-Al 2 O 3 micro-powder as raw materials. The effect of α-Al 2 O 3 content on the microstructures, mechanical properties and purification efficiency of MgO-based filters were investigated via SEM, EDS, and immersion test in molten steel, etc. The results indicate that the reactive sintering between α-Al 2 O 3 and MgO promoted the formation and growth of neck connections of magnesium aluminate spinel between grains, increased the density of the filter skeleton, and decreased the pore size inside the skeleton. The higher density and smaller pore size of the skeleton, as well as the neck connection of spinel and crack deflection effect caused by magnesium aluminate spinel, comprehensively improved the strength and thermal shock resistance of MgO-based ceramic filters. Furthermore, the results from the immersion test in molten steel revealed that an appropriate amount of high-temperature liquid phase, smaller pore size, and in-situ generated spinel were beneficial for the filters to adsorb dissolved aluminum, dissolved oxygen, alumina inclusions, and secondary spinel inclusions in the steel. The filter with 20 wt.% α-Al 2 O 3 had the best overall performance with a compressive strength of 2.35 MPa, a compressive strength after thermal shock test of 1.91 MPa and an efficiency of 77.3% in reducing the total oxygen content of the steel.
materials science, ceramics