Abstract:Ferric pyrophosphate (FePP) was added to an ammonium polyphosphate (APP)-pentaerythritol (petol) intumescent flame retardant (IFR) system in polypropylene (PP) matrix, with subsequent investigation into the synergistic effect between FePP and the IFRs. Limited oxygen index (LOI), UL-94 test and cone calorimeter test were employed to study the flame retardance of the synthesized flame retardant PP composites. Thermogravimetric analysis (TGA) and thermogravimetric analysis-infrared spectrometry (TG-IR) were used to study their thermal degradation characteristics and gas products. TG-IR results demonstrate that there is no Fe (CO)(5) produced from PP/IFR/FePP system, which implies that the flame retardant mechanism of PP/IFR/FePP system is in the condensed phase rather than in the gas phase. Real time FTIR and X-ray photoelectron spectroscopy (XPS) were used to monitor the thermal oxidative stability and the high temperature performance of the flame retardant PP composites. The real time FTIR spectra show that all peaks around 2900 cm(-1) almost disappear at 380 degrees C for the PP/IFR system, meaning that PP decomposes completely at this temperature. But after the addition of 2 wt% wt% FePP, the peaks still exist till 400 degrees C. XPS shows that the aliphatic carbon atom content in PP/23 wt% wt% IFR/2 wt% wt% FePP (63.8%) is much higher than the one without FePP, and the total oxygen atom content in PP/23 wt% wt% IFR/2 wt% wt% FePP is just 19.1%, while the one in PP/25 wt% IFR is as high as 35.7%. Copyright (C) 2009 John Wiley & Sons, Ltd.

Preparation and properties of FR-PP with phosphorus-containing intumescent flame retardant

The mechanical properties and thermal performances of polypropylene with a novel intumescent flame retardant

Flame Retardation and Thermal Degradation of Intumescent Flame‐retarded Polypropylene Composites Containing Spirophosphoryldicyandiamide and Ammonium Polyphosphate

A Novel Halogen‐free Intumescent Flame Retardant Containing Phosphorus and Nitrogen and Its Application in Polypropylene Systems

A phosphorus-, nitrogen- and carbon-containing polyelectrolyte complex: preparation, characterization and its flame retardant performance on polypropylene

Synthesis and application in polypropylene of a novel of phosphorus-containing intumescent flame retardant.

Flammability and Thermal Properties of a Novel Intumescent Flame Retardant Polypropylene

Modification of Intumescent Flame Retardant by Phosphorus Containing Titanate Coupling Agent and Its Application in Polypropylene

Study on PP Flame Retarded with Aryl Phosphate and Intumescent Flame Retardant Compound

Preparation and Flame Retardancy of Intumescent Flame-Retardant Polypropylene

Flame Retardancy and Thermal Degradation of Intumescent Flame Retardant Polypropylene with Mp/Tpmp

Preparation and properties of flame retardant polypropylene with an intumescent system encapsulated by thermoplastic polyurethane

Study on the Mixture of an Intumescent Flame Retardant Containing Various Caged Phosphates Melamine Salt and PP

Synthesis and Application of a Mono-Component Intumescent Flame Retardant for Polypropylene

A novel highly efficient intumescent flame-retardant polypropylene: Thermal degradation, flame retardance and mechanism

A new intumescent flame-retardant: preparation, surface modification, and its application in polypropylene

Synergistic Effect of Phosphorus-Containing Montmorillonite with Intumescent Flame Retardant in Polypropylene

Synergistic effects of ferric pyrophosphate (FePP) in intumescent flame-retardant polypropylene

Preparation and properties of a single molecule intumescent flame retardant

Great enhancement of efficiency of intumescent flame retardants by titanate coupling agent and polysiloxane

Studies on Synergistic Effect of α-zirconium Phosphate in Intumescent Flame Retarded Polypropylene Composites