High Filterable Electrospun Nanofibrous Membrane with Charged Electret After Electrification Treatment for Air Filtration
Bo Yang,Ming Hao,Zheng Huang,Zhijun Chen,Yanbo Liu
DOI: https://doi.org/10.1007/s12221-023-00110-1
IF: 2.5
2023-02-22
Fibers and Polymers
Abstract:Conventionally, charged melt-blown nonwoven fabrics had been applied as filter media in various protective masks and high-temperature gas filters in relevant fields, which are featured with high filtration efficiency (FE) and low pressure drop (ΔP). The charges, however, and hence the filtration efficiency tend to decay with extended time, elevated temperature and increased humidity. In the current study, three types of charged nanofibrous membrane-based filtration medias, i.e., charged polyvinylidene fluoride (PVDF), polytetrafluoroethylene-PVDF, and tourmaline-PVDF electrospun nanofibrous membranes (ENMs), were successfully prepared by electrospinning process, followed by electrification. The resultant samples showed excellent filtration performance, relatively durable charging effect, and stable air permeability. Moreover, the data of FE and ΔP of ENMs after exposure to the air for 12 h are still more than 98% and less than 100 Pa, respectively. The combined method of electrospinning technology and electrification was proposed to obtain novel filter medias having semi-durable FE and relatively low ΔP, i.e., the FE will still remain at a relatively high level even if all the charges escape away from the nanofiber-based filter media, which may find wide applications in gas filtration industry.
materials science, textiles,polymer science