Abstract:The results of two sets of experiments to measure the elastic-plastic behaviour of gold at the nanometre length scale are reported. One set of experiments was on free-standing nanoscale single crystals of gold, and the other was on freestanding nanoscale specimens of open-celled nanoporous gold. Both types of specimens were fabricated from commercially available leaf which was either pure Au or a Au/Ag alloy following by dealloying of the Ag. Mechanical testing specimens of a 'dog-bone' shape were fabricated from the leaf using standard lithographic procedures after the leaf had been glued onto a silicon wafer. The thickness of the gauge portion of the specimens was about 100 nm, the width between 250 nm and 300 nm and the length 7 mu m. The specimens were mechanically loaded with a nanoindenter (MTS) at the approximate midpoint of the gauge length. The resulting force-displacement curve of the single crystal gold was serrated and it was evident that slip localization occurred on individual slip systems; however, the early stages of the plastic deformation occurred in a non-localized manner. The results of detailed finite element analyses of the specimen suggest that the critical resolved shear stress of the gold single crystal was as high as 135 MPa which would lead to a maximum uniaxial stress of about 500 MPa after several per cent strain. The behaviour of the nanoporous gold was substantially different. It exhibited an apparent elastic behaviour until the point where it failed in an apparently brittle manner, although it is assumed that plastic deformation occurred in the ligaments prior to failure. The average elastic stiffness of three specimens was measured to be E-np = 8.8 GPa and the stress at ultimate failure averaged 190 MPa for the three specimens tested. Scaling arguments suggest that the stress in the individual ligaments could approach the theoretical shear strength.

Determination of the Elastic Constants of Gold Nanorods Produced by Seed Mediated Growth

Extensional Vibration and Size-Dependent Mechanical Properties of Single-Crystal Gold Nanorods

Ultrafast Laser-Excited Vibration and Elastic Modulus of Individual Gold Nanorods

Breathing Mode Vibrations and Elastic Properties of Single-Crystal and Penta-Twinned Gold Nanorods.

Growth and Overgrowth of Concentrated Gold Nanorods: Time Resolved Saxs and Xanes

Vibrations of single-crystal gold nanorods and nanowires

Strong Hall-Petch Type Behavior in the Elastic Strain Limit of Nanotwinned Gold Nanowires

Strain mapping in symmetrical core-shell gold nanorods from HRTEM images

Plastic Deformation in Nanoscale Gold Single Crystals and Open-Celled Nanoporous Gold

Ultrafast Laser-Induced Premelting and Structural Transformation of Gold Nanorod

In Situ Observations Reveal the Five-fold Twin-Involved Growth of Gold Nanorods by Particle Attachment

Quasi-Two-Dimensional Gold Nanosheets with Ultrahigh Strength

Shape-dependent local strain in gold nanorods: data-driven atomic-resolution electron microscopy analysis

First-principles density functional theory (DFT) study of gold nanorod and its interaction with alkanethiol ligands

One-Step Synthesis of Large-Aspect-Ratio Single-Crystalline Gold Nanorods by Using Ctpab and Ctbab Surfactants

Electronic structure at nanocontacts of surface passivated CdSe nanorods with gold clusters

The Role of Polytetrahedral Structures in the Elongation and Rupture of Gold Nanowires

Spontaneous room temperature elongation of CdS and Ag2S nanorods via oriented attachment

Investigation of pH effect on gold nanorod synthesis

Microfabrication and Mechanical Properties of Nanoporous Gold at the Nanoscale

Mechanical Properties and Scaling Laws of Nanoporous Gold