Study On Structure And Corrosion Resistance Of Micro Arc Oxidation Black Ceramic Coatings On Aluminum Alloy

Wu Zhendong,Jiang Zhaohua,Yao Zhongping,Wang Zhijiang,Zhang Xuelin
DOI: https://doi.org/10.3321/j.issn:1002-185x.2007.z2.198
2007-01-01
Rare Metal Materials and Engineering
Abstract:In an electrolyte of sodium polyphosphate and the additive containing chromium solution, black ceramic coatings were prepared on LY12 Al-alloy substrate through the micro arc oxidation (MAO) technique. The composition, microstructure and the corrosion resistance of coatings were investigated by X-ray diffraction, scanning electron microscopy and electrochemical analyzer. The coating thickness is increased linearly with increasing time; and the additive is helpful for the increase of the coating thickness somehow. There are lots of unclosed discharge channels on the coating surface. The black color of the coatings become deeper and deeper from the interface to the surface. Within the coating, the content of Cr increases from the interface to the surface, while the content of Al and Cu decreases. The phase composition in the coating prepared with additive is composed of alpha-Al2O3 and a little gamma-Al2O3, but phase compositions in the coating prepared without additive is composed of gamma -Al2O3 and the coating color is ivory-white. The corrosion resistance of the coated samples is better than that of the substrate and the corrosion resistance of the black coating containing Cr is increased to a large extent.
What problem does this paper attempt to address?