Structural and Dielectric Properties of Nickel-Doped and Lanthanum-Chromium-Doped Barium Titanate Ceramics

Mamoru Fukunaga,Guobao Li,Yoshiaki Uesu,Kay Kohn

DOI: https://doi.org/10.1143/JJAP.41.6926

2002-01-01

Abstract:Nickel-doped BaTiO3 (BaTi1-yNiyO3-delta: BTN) and lanthanum-chromium double-doped BaTiO3 (Ba1-xLaxTi1-xCrO3: BLTC) ceramics were synthesized and their symmetry and dielectric properties were studied. Samples were sintered at 1400degreesC in air from stoichiometric amounts of BaCO3 and other metal oxides. X-ray diffraction data were obtained at 20degreesC. Dielectric properties were measured in the temperature range of 18 K to 453 K. With the increase of dopant ratio y, Curie temperature T-C of BTN decreases, but when y exceeds about 0.01, a hexagonal phase appears and the dielectric constant becomes smaller. On the other hand, in the entire range of x, BLTC shows a perovskite structure and the compounds with larger x exhibit conductive rhombohedral or orthorhombic phases. In the range of x smaller than 0.1, BLTC shows a diffuse phase transition and a high dielectric constant with small tan delta. The relaxor-like frequency dispersion was observed in BLTC at low temperatures.