Abstract:To investigate the carbonation regularity in concrete of 100mm×100mm×400mm, in the environment, (20±3)% (volume fraction) concentration of CO2, (70±5)% relative humidity and (20±2)°C temperature. The concrete specimens were divide into two parts: curing 28dayswith temperature of (20±2)°C and the relative humidity ⩾95% (named wet curing), and then curing for 3years (named A condition) with the relative humidity of (60±5)% and the temperature of (20±2)°C (named dried curing) and long-age wet curing for 90days (named B condition). The water-binder ratio was 0.37, 0.45 and 0.53, the content of fly ash substituting for the equal quality of cement by mass was 0%, 30% and 60%, respectively. Based on the scanning electron microscope (SEM) morphology of the interfacial transition zone of concrete’s coarse aggregate and X-ray diffraction (XRD) analysis, the influence mechanism of wet curing for 90days on the fly ash concrete carbonation resistance ability was analyzed. The results show that the wet curing for 90days had the positive effect of dense interfacial zone and the negative effect of calcium hydroxide consumption on the concrete carbonation resistance ability. In the case of high fly ash content with low water-binder ratio or low fly ash content with high water-binder ratio, the dense effect of the interfacial transition zone of concrete’s coarse aggregate occupied a dominant position, and the carbonation resistance ability was greatly improved after wet curing for 90days. The average increment value of carbonation depth of fly ash concrete in each group decreased by 53.5% compared with the specimens cured under A condition. When the water-binder ratio and the fly ash content were either higher or lower, the positive effect of dense interfacial zone and the negative effect of calcium hydroxide consumption had little significant effect on the concrete carbonation resistance ability, and the wet curing for 90days had no obvious influence on improving the carbonation resistance ability. At present, the average increment value of carbonation depth of fly ash concrete in each group decreased only by 11.5% of that under A condition.

RESEARCH ON 2-DIMENSION,3-DIMENSION CARBONATIONS AND SUPERPOSITION COEFFICIENT OF FLYASH CONCRETE

2D and 3D carbonation of fly ash concrete

Reviews on the models and test Methods of Concrete Carbonation and some suggestions

Carbonation Depth Prediction of Fly Ash Concrete Subjected to 2-and 3-Dimensional CO 2 Attack

STUDY ON CARBONATION OF FLY ASH CONCRETE WITH FREEZE-THAW CYCLE

1D and 2D carbonation of fly ash concrete under flexural stress

Multi-dimensional carbonation and service life prediction model of fly ash concrete subjected to flexural stress and CO2 attack

Carbonation depth model and carbonated acceleration rate of concrete under different environment

A Reaction-Diffusion Modeling of Carbonation Process in Self-Compacting Concrete

Numerical Simulation on Carbonation Depth of Concrete Structures considering Time- and Temperature-Dependent Carbonation Process

Influence of Fly Ash Dosage and Desert Sand Replacement Ratio (DSRR) on the Carbonation Resistance of Concrete

Overview the mechanism and forecast model of concrete carbonization

STRESS-CARBONATION OF FLY ASH CONCRETE

Long-Age Wet Curing Effect on Performance of Carbonation Resistance of Fly Ash Concrete

Research on Chloride 2 Dimensions, 3 Dimensions Diffusion of Concrete

Effecting Coefficients for Concrete Structure Durability Design Index

Two-and Three-Dimensional Chloride Ingress into Fly Ash Concrete

Carbonation Process Simulation for Cement-Based Materials Based on Microstructure by a Cement Hydration Model

EXPERIMENTAL STUDY ON CARBONATION PROPERTIES OF CONCRETE BASED ON BENDING LOAD DAMAGE

Effects of Micro-Environmental Climate on the Carbonation Depth and the Ph Value in Fly Ash Concrete

Study of concrete carbonation depth measured by using different color reagents