Precipitate microstructures, mechanical properties and corrosion resistance of Al-1.0 wt%Cu-2.5 wt%Li alloys with different micro-alloyed elements addition
Dan-yang Liu,Yun-long Ma,Jin-feng Li,Rui-feng Zhang,Hideaki Iwaoka,Shoichi Hirosawa
DOI: https://doi.org/10.1016/j.matchar.2020.110528
IF: 4.537
2020-09-01
Materials Characterization
Abstract:<p>The evolution of precipitate microstructures of the Al-1.0wt%Cu-2.5wt%Li alloys with different micro-alloyed elements addition was investigated during ageing at 175 °C together with the mechanical properties and corrosion resistance. It was found that the Al-Cu-Li alloy with Zn addition possesses not only higher yield strength but also improved intergranular corrosion resistance, compared with the alloy with Mg addition. The corresponding precipitate microstructures were greatly affected by Zn or Mg micro-alloyed element addition, for example, with Zn addition the δ′-Al<sub>3</sub>Li, T<sub>1</sub>-Al<sub>2</sub>CuLi and θ′-Al<sub>2</sub>Cu (and θ″) phases were formed within grains, whereas the coarse T<sub>B</sub>-Al<sub>7</sub>Cu<sub>4</sub>Li phase and the T<sub>1</sub> phases appeared at grain boundaries (GBs). In contrast, the Al-Cu-Li alloy with Mg addition possessed the δ′, T<sub>1</sub> and S′-Al<sub>2</sub>CuMg phases within grains, while the coarse AlCu phase and T<sub>1</sub> phases were present at GBs. The alloy with combined Zn + Mg addition exhibited a duplex microstructure of the two alloys, resulting in lower mechanical strengths but the intermediate corrosion resistance. Therefore, the increased amount of Zn-containing coarsened T<sub>B</sub> phase at GBs was found to improve the corrosion resistance of the alloy with Zn addition, due to the smaller potential difference between the GB precipitates and the adjacent zones.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing