Preparation of Polymeric Nanosilica Hybrid Materials and Their Properties

Ma Guozhang,Liu Wei,Yan Tao,Wei Liqiao,Xu Bingshe

DOI: https://doi.org/10.3724/sp.j.1105.2011.10031

2011-01-01

Acta Polymerica Sinica

Abstract:The nanosilica with-NCO on the surface was prepared,using of the characteristic-OH on the surface of nanosilica could react with IPDI,which was further reacted with HEA,the ploymerizable nanosilica hybrid particle was prepared.The nanosilica and modified nanosilica were characterized with FTIR,TGA and SEM.The results indicated that IPDI and HEA had been grafted on the surface of nanosilica with chemical bond form and the grafting ratio was 37.29%,the dispersibility of grafted nanosilica was better than that of unmodified nanosilica,the aggregation phenomena was improved.Compared with the coating with unmodified nanosilica,the UV curable coating with the same ratio nanosilica hybrid material had lower viscosity and faster CC double bonds conversion,the hardness of the curable film was improved obviously.