Study on the preparation,characterization and performance of TiO2-N-S photocatalyst

于秀娟,程修文,杨莉莎
2011-01-01
Abstract:Nitrogen and sulfur co-doped TiO2 photocatalyst(label as TiO2-N-S) was prepared by a sol-gel process using cystine as doping agent.The samples were characterized by the methods of X-ray powder diffraction(XRD),transmission electron microscopy(TEM),scanning electron microscopy(SEM),X-ray photoelectron spectroscopy(XPS) and surface photovoltage spectrum(SPS) and the performance of the samples was tested by degradation for phenol solution under simulated sunlight irradiation.XRD analysis showed that the as-prepared modified-catalyst was absolute anatase and co-doping with nitrogen and sulfur could efficiency restrain the growth of crystalline grain and enhance the temperature of phase transformation.XPS analysis displayed that sulfur existing as cationic S6+ by replacing Ti4+ and the structure of nitrogen was broadening which could be attributed to the formation of O—Ti—N and Ti—N—O and also the content of the surface hydroxyl groups was remarkable increased.The light absorption band edge of TiO2-N-S in the visible-light region was clearly observed according to SPS analysis.Under the simulated sunlight irradiation with 120min,the 79.3% degradation rate of phenol could be achieved.
What problem does this paper attempt to address?