Abstract:Bi2Te3-based compounds are currently the most commercially relevant thermoelectric materials near room temperature. They are prepared via hot pressing, hot deformation, spark plasma sintering, and other consolidation processes, which are typically performed at 400–500 °C. Such high-temperature processes are energy-intensive and generate unnecessary waste heat, making them undesirable for a large-scale production. In this study, a low-temperature liquid-phase-assisted sintering (or so-called cold-sintering) process was employed to fabricate p-type Bi0.5Sb1.5Te3 bulk materials at temperatures below 150 °C. At the optimal sintering temperature (130 °C), a ZT value as high as 0.56 at 450 K can be achieved, competitive to that of a commercial Bi0.5Sb1.5Te3 ingot (ZT 0.8–1.0). The addition of a small amount of transient liquid facilitates grain reorientation and expedites a mass transfer process under axial compaction and liquid evaporation conditions, thus resulting in nearly fully densified Bi0.5Sb1.5Te3 pellet samples (>97% theoretical density). Furthermore, the low-temperature sintering process results in the reduction of grain size and promotes twin boundaries, resulting in a low lattice thermal conductivity of 0.57 W m–1 K–1 at 380 K due to phonon scattering. The strategy reported in this work can be used not only as a substitute for high-temperature sintering of other thermoelectric materials but also to engineer phonon scattering for high-performance thermoelectrics.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c03540.Single parabolic band model and calculated transport properties; EBSD analysis for pellet sintered at 110 °C; BSE, EDS mapping, and TEM images of pellet sintered at 130 °C; average ZT values; and XPS results (PDF)This article has not yet been cited by other publications.

Sonochemical Synthesis of Nanocrystalline Bi2Te3 Thermoelectric Compounds

The reaction mechanism for the synthesis of Bi2Te3-based thermoelectric materials by aqueous chemical method

Ultrasonic-assisted Hot Pressing of Bi2Te3-based Thermoelectric Materials

Synthesis and Thermoelectric Properties of Bi2te3 Based Nanocomposites

Solvothermal Preparation and Characterization of Nanocrystalline Bi2te3 Powder with Different Morphology

Microwave-assisted Synthesis of Nanocrystalline Bi2Te3

Thermoelectric Bi2Te3 nanotubes synthesized by low-temperature aqueous chemical method

Synthesis and thermoelectric characterization of Bi2Te3 nanoparticles

Nanostructuring and improved performance of ternary Bi–Sb–Te thermoelectric materials

Size-controllable Sonochemical Synthesis of Thermoelectric Material of Bi2Se3 Nanocrystals

Solvothermal Synthesis and Characterization of Bi2Te3 Nanocrystals

Development of Nanostructured Bi2Te3 with High Thermoelectric Performance by Scalable Synthesis and Microstructure Manipulations

Characterization of nanocrystalline bismuth telluride (Bi2Te3) synthesized by a hydrothermal method

Novel thermoelectric Bi2Te3 nanotubes and nanocapsules prepared by hydrothermal synthesis

Effect of solvent on the microstructures of nanostructured Bi 2Te3 prepared by solvothermal synthesis

Solvothermal synthesis of nanostructured Bi_2Te_3 based thermoelectric materials

Nanostructured Bi2Te3 Synthesized by Low Temperature Aqueous Chemical Route

Cold-Sintered Bi 2 Te 3 -Based Materials for Engineering Nanograined Thermoelectrics

Effects of Hydrothermaly Synthesized Sb_2Se_3 Nanowires on the Thermoelectric Properties of Bi_2Te_3 Nanopowders

Solvothermal preparations of nanocrystalline Bi2Te3 powders

Ultrasonic Synthesis of Nanocrystals of Metal Selenides and Tellurides