Nanoporous Zero-Valent Iron

Cao Jiasheng,Clasen Patrick,Zhang Wei-xian

DOI: https://doi.org/10.1557/jmr.2005.0401

2005-01-01

Abstract:Hollow and nanoporous particles of zero-valent iron (ZVI) were prepared with template-directed synthesis. Polymer resin beads (0.4 mm diameter) were coated with nanoscale iron particles by reductive precipitation of ferrous iron [Fe(II)] with sodium borohydride. The resin was calcinated at 400 °C to produce hollow and nanoporous iron spheres. The nanoporous iron oxides were then reduced to metallic iron by hydrogen at 500 °C. Scanning electron microscope images of the reduced iron spheres showed that the particles were hollow. The shell thickness was approximately 5 μm and highly porous. Brunauer–Emmett–Teller specific surface area was 2100 m 2 /kg. In comparison, the theoretical specific surface area of solid iron particles of the same size is just 1.9 m 2 /kg. Batch tests showed that the surface area normalized reactivity of the porous particles were 14–31% higher than microscale iron particles with similar surface areas for the transformation of hexavalent chromium [Cr(VI)], azo dye Orange II (4-[(2-hydroxyl-1-naphthalenyl)azo]-benzenesulfonic acid monosodium, and trichloroethene. The combined performance enhancement (larger surface area and higher surface activity) is significant (>1200 times).