Abstract:For typical biodegradable polymers, their overall performance almost declines exponentially to the degradation degree, which inevitably leads to a dilemma between the requirements of service life and retention time in the environment (both in vitro and in vivo ). It is a great challenge to develop a biodegradable polymeric device with relatively stable performance in service while rapidly degrading out of service. Herein, we demonstrate an effective strategy to control degradation of biodegradable polymers in stages by constructing separated bicontinuous microphases with very different microphase degradation rates. First, polyurethane copolymers (PCL-b-CrP-U) containing two blocks, i.e. , semicrystalline poly(ε-caprolactone) (PCL) blocks and amorphous random copolymer blocks (CrP) based on ε-CL and p -dioxanone (PDO), were synthesized. The microscopic morphology of PCL-b-CrP-U is investigated by an alkali-accelerated degradation experiment, which also demonstrates that the chain cleavage-induced crystallization during degradation resulted in a self-reinforcement by forming degradation residues with a scaffold-like morphology. The tensile test shows that PCL-b-CrP-U has excellent mechanical properties (1500% of elongation at break, a tensile strength of about 7.5 MPa, and an elastic modulus of 40.0 MPa). The degradation experiments with artificial pancreatic juice as a working medium reveal that PCL-b-CrP-U samples containing relatively high PDO units exhibit a three-stage degradation, i.e. an induction stage, a steady degradation stage and an accelerated degradation stage. The CrP phase preferentially hydrolyzes to form some microchannels due to its amorphous nature and relatively high hydrophilicity, effectively accelerating the entry of water and enzymes into the inner parts of the sample. Meanwhile, at this stage, those originally amorphous PCL segments gradually crystalize owing to their enhanced chain mobility induced by the chain cleavage, forming a "scaffold"-like structure, which effectively reinforces the sample to resist the damage from external force and therefore guarantees a relatively stable mechanical performance of PCL- b -CrP-U during service. With the further depletion of the CrP phase, the intermediate "scaffold"-like structure is also very beneficial to accelerate the degradation of residues owing to its large specific surface area, which is expected to be beneficial for preventing long-term retention of the implantation devices.

Biodegradation of polycarbonate polyurethane

Hydrolytic Degradation Of Biobased Poly(Butylene Succinate-Co-Furandicarboxylate) And Poly(Butylene Adipate-Co-Furandicarboxylate) Copolyesters Under Mild Conditions

The in Vitro and in Vivo Stability of Poly(urethaneurea)s As Biomedical Materials

Synthesis, Characterization and Biocompatibility of Biodegradable Elastomeric Poly(ether-ester Urethane)s Based on Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) and Poly(ethylene Glycol) Via Melting Polymerization

Toward regulating biodegradation in stages of polyurethane copolymers with bicontinuous microphase separation

Characterization, biodegradability and blood compatibility of poly[(R)-3-hydroxybutyrate] based poly(ester-urethane)s.

Synthesis and properties of biodegradable poly(ester-urethane)s based on poly(ε-caprolactone) and aliphatic diurethane diisocyanate for long-term implant application: effect of uniform-size hard segment content

Performance Study of Biodegradable Polyurethanes from Different Biodicarboxylic Acids and Their Potential Applications

In vitro and in vivo degradation behavior of n-HA/PCL-Pluronic-PCL polyurethane composites

The Mechanical Properties and in Vitro Biodegradation and Biocompatibility of Uv-Treated Poly(3-Hydroxybutyrate-Co-3-Hydroxyhexanoate)

Biocompatibility of poly(carbonate urethane)s with various degrees of nanophase separation

Synthesis, phase behavior, and simulated in vitro degradation of novel HTPB-b-PEG polyurethane copolymers

Synthesis and characterization of biodegradable polyurethanes based onL-cystine/cysteine and poly(ϵ-caprolactone)

Shape Memory Properties And Enzymatic Degradability Of Poly(Epsilon-Caprolactone)-Based Polyurethane Urea Containing Phenylalanine-Derived Chain Extender

Synthesis And Characterization Of Biodegradable Polyurethanes Based On L-Cystine/Cysteine And Poly(Epsilon-Caprolactone)

The Main Chain Biodegradable Polyurethane with Anti-protein Adsorption and Anti-bacterial Adhesion Performances

Synthesis and Properties of Degradable Medical Polyurethane with L-Lysine Ethyl Ester Diisocyanate as Hard Segment

In Vitro Biocompatibility and Degradation of Terpolyester 3Hb-Co-4hb-co-3hhx, Consisting of 3-Hydroxybutyrate, 4-Hydroxybutyrate and 3-Hydroxyhexanoate.

Biodegradable injectable polyurethanes: synthesis and evaluation for orthopaedic applications

Development of Arg-Based Biodegradable Poly(ester Urea) Urethanes and Its Biomedical Application for Bone Repair

High Modulus Biodegradable Polyurethanes for Vascular Stents: Evaluation of Accelerated in vitro Degradation and Cell Viability of Degradation Products