Abstract:The morphology-controlled synthesis of SnO2 hollow/nanoporous nanostructures (nanotubes, urchin-like morphologies and nanospheres) was achieved via a template-engaged replacement reaction at a mild temperature (lower than 80 degrees C). The formation mechanism of hollow interior and nanoporous walls for the obtained SnO2 nanostructures (SnO2 nanotubes were used as an example) was investigated based on TEM and HRTEM observations during different reaction stages. It is found that bridge voids firstly form at the MnO2/SnO2 interface, followed by the inward development of voids before the MnO2 core is completely consumed. Two types of short-circuited galvanic cells, MnO2/Mn2+ rSnO(2)/Sn2+ and concentration cell-SnO2/Sn2+ (interior) rSnO(2)/Sn2+ (exterior), are probably responsible for the formation of SnO2 nanotubes and outward growth of SnO2 along MnO2. Moreover, the calculation result of the outer diameter of SnO2 nanotubes is in good agreement with the observation results by SEM and TEM. When evaluated as anodes for lithium ion batteries (LIBs), the three SnO2 nanostructures exhibit superior rate capability and cycling performance. Especially, SnO2 nanotubes present the best rate capability: specific capacities of above 800 mA h g(-1) at 200 mA g(-1) and about 500 mA h g(-1) at 4000 mA g(-1) were achieved, respectively. Importantly, the 1D morphology of SnO2 nanotubes can be well preserved after prolonged cycling at a relatively high current density, indicating good structural stability of the resulting nanotubes during the Li+ insertion/extraction process. These results indicate that the obtained SnO2 hollow/nanoporous nanostructures would be promising anode materials for next-generation LIBs.

Fabrication of porous BaSnO3 hollow architectures using BaCO3@SnO2 core–shell nanorods as precursors

Self-templated Porous Hierarchical SnO2 Ceramics with Enhanced Lithium Storage Capacity

Facile Fabrication of Porous ZnO by a Template Free Method

Metal oxide and sulfide hollow spheres: layer-by-layer synthesis and their application in lithium-ion battery.

Layer-by-layer synthesis of γ-Fe2O3@SnO2@C porous core-shell nanorods with high reversible capacity in lithium-ion batteries.

Synthesis of Co3O4@SnO2@C core-shell nanorods with superior reversible lithium-ion storage

Self-templating synthesis of SnO2-carbon hybrid hollow spheres for superior reversible lithium ion storage.

Core-Shell ZnO@SnO2 Nanoparticles for Efficient Inorganic Perovskite Solar Cells.

Large-scale low temperature fabrication of SnO2 hollow/nanoporous nanostructures: the template-engaged replacement reaction mechanism and high-rate lithium storage.

Mesoporous Single-crystal CoSn(OH)6 Hollow Structures with Multilevel Interiors

Controllable synthesis of recyclable core-shell γ-Fe2O3@SnO2 hollow nanoparticles with enhanced photocatalytic and gas sensing properties

Preparation and optoelectronic properties of hierarchical porous zno microspheres

Β-Pbo2 Hollow Nanostructures from the Complex Precursor: A Self-Produced Intermediate Template Route

Use of Carbonaceous Polysaccharide Microspheres As Templates for Fabricating Metal Oxide Hollow Spheres

The Preparation of Uniform Sno2 Nanotubes with A Mesoporous Shell for Lithium Storage

Chemical Prelithiation/Presodiation Strategies Toward Controllable and Scalable Synthesis of Microsized Nanoporous Tin at Room Temperature for High‐Energy Sodium‐Ion Batteries

Preparation of Nanowire Arrays of Amorphous Carbon Nanotube-Coated Single Crystal SnO<sub>2</sub>

An anion-exchange strategy for 3D hierarchical (BiO)2CO3/amorphous Bi2S3 heterostructures with increased solar absorption and enhanced visible light photocatalysis

Facile Synthesis, Sintering, and Optical Properties of Single-Nanometer-Scale SnO2 Particles with a Pyrrolidone Derivative for Photovoltaic Applications

Ultrathin SnO 2 nanosheets: Oriented attachment mechanism, nonstoichiometric defects, and enhanced lithium-ion battery performances

Preparation of SnO Nanoshells with Enhanced Lithium-Storage Properties.