Fabrication of Transparent Wear-Resistant Superhydrophobic SiO2 Film Via Phase Separation and Chemical Vapor Deposition Methods
Jiawei Zheng,Jinchuan Yang,Wen Cao,Yue Huang,Zhonghua Zhou,Ya-Xi Huang
DOI: https://doi.org/10.1016/j.ceramint.2022.07.154
IF: 5.532
2022-01-01
Ceramics International
Abstract:Glass with superhydrophobic, transparent, and wear-resistant properties are quite desirable for the applications in high building glass curtain, wind shield glass, and solar cell cover glass. How to fabricate a superhydrophobic surface with both high transparency and good wear resistance is still a great challenge because roughness and transparency are mutually exclusive. Here, transparent, wear-resistant, superhydrophobic inorganic coating on glass substrate has been successfully achieved by a two-step process combining phase separation and chemical vapor deposition (CVD). Firstly, a wear-resistant inorganic porous film with honeycomb-shaped pores is prepared on the glass surface by applying the phase separation method based on the epoxy resin-silica sol system. The prepared porous structure is used as the micron-level "armor" protective structure. Then nano-SiO2 particles have been deposited on the porous film via CVD method to construct a micro-nano hierarchical structure required for superhydrophobicity on the glass surface. Finally, a superhydrophobic film has been successfully achieved after being modified with fluoroalkylsilane (FAS). The water contact angle (WCA) and water sliding angle (WSA) of the obtained sample are 154.0 +/- 0.9 degrees and 3.2 +/- 0.2 degrees, respectively. At the same time, it has good transparency with high visible light transmittance and low haze. Its visible light transmittance is as high as 87.7% (only 1.7% less than blank glass) and haze is only 1.87%. Moreover, after 2000 cycles of abrasion under harsh conditions, the film still maintains good hydrophobic properties, and its water contact angle is still higher than 130 degrees. In addition, the prepared functional film also has excellent self-cleaning performance, as well as acid and salt corrosion resistance. The preparation method used here has the advantages of low cost, easy operation, large area preparation, and broad application prospects.