Abstract:To replace the surface treatment process by phosphating and saponification, a coating was prepared on the surface of low carbon steel sample by dipping method using water-based polymer mixed lubricant. Using HT500 ball-disk wear tester, tribological behaviors of low-carbon steel were investigated under three different lubricating conditions such as polymer mixed lubricant coating, film by Phosphating and saponification, and non-lubricants. Friction shear stress on the dry friction contact surface was also analyzed. The morphology of the worn surface was observed by VHX-600K super depth of focus microscope, and the wear mechanism was studied. The results show that the polymer mixed lubricant coating has the effect of lubricating and antifriction which is similar to film by phosphating and saponification. Compared with the dry friction, the friction coefficient decreases by 67.33% and 68.79%, respectively, the former is slightly lower by 2.1% within 5 min of the initial friction, and the antifriction performance of both are steady relatively in the test. Additionally, friction and wear mechanism is related to friction behaviors under different lubricating conditions. In the dry friction process, the abrasive wear and oxidation wear play the leading role, and the wear mechanism of film by phosphating and saponification on the metal surface is slight abrasive wear and little oxidation wear, and the surface wear is the lightest under the polymer mixed lubricant coating while the wear mechanism is mainly slight abrasive wear.

Effect of X-1P as Additive on the Tribological Behavior of Potassium Stearate Films

Tribological Performance of Stearic Acid Film on Textured 45# Steel Substrate

Xps and Xanes Characteristics of Tribofilms and Thermal Films Generated by Two P- And/Or S-Containing Additives in Water-Based Lubricant

The Effect of Solid-Liquid Composite Lubrication on the Tribological Properties of Bearing Steel

Tribological Behaviors and Film Analysis of Two Ashless Phosphorus/Sulfur-Containing Additives in Rapeseed Oil

Effects Of Polymer Composited Lubricant Coating On Tribological Properties Of Low-Carbon Steel Surface

Effect of Ag Content on Microstructure and Tribological Performance of WS2–Ag Composite Films

Tribochemical Behaviors of Phosphite Esters and Their Combinations with Alkyl Amines

Tribological Properties and Worn Surface Analysis Generated by Ashless and Phosphorus-Free Additive in Water-Based Lubricant

Tribological Study of A Novel Borate Ester Containing S, P with High Hydrolytic Stability As A Multifunctional Lubricating Additive

Comparative tribological and friction behaviors of oil-lubricated manganese phosphate conversion coatings with different crystal sizes on AISI 52100 steel

Synergistic Effects between Plasma-Nitrided AISI 52100 Steel and Zinc Dialkyldithiophosphate Additive under Boundary Lubrication

X‐ray Absorption Near‐edge Structure Analysis of Tribofilms Generated by Highly Efficient, Friction‐reducing Additive in Water–polyglycol–glycol Lubricant

XANES characteristics of tribofilms generated by dithiophosphate additive in water at different test temperatures and durations

Tribological Performance and Wear Mechanism of Compound Containing S, P, and B as EP/AW Additives in Copper Foil Oil

Effect of Natural Attapulgite Powders As Lubrication Additive on the Friction and Wear Performance of A Steel Tribo-Pair

Effectively improving the extreme-pressure capacity of a class of intercalated zirconium phosphate materials

Tribological Properties of Phosphorus and Sulfur-Free Organotungstate Additive on Plasma Nitrided Surface of Bearing Steel

The Tribological Chemistry of a Novel Borate Ester Additive and Its Interaction with ZDDP Using XANES and XPS

Tribological Behaviour of Three S-Containing Triazine Derivatives and Their Synergetic Effect with Zinc Dialkyldithiophosphate As Additives

Preparation and Tribological Behavior of the End Hydroxyl Group Phenyl-containing Poly Silicone Film