Abstract:In order to further improve the properties of the A356 (Al–7Si–0.3Mg) alloy, which is widely used due to its excellent properties, the effect of alloying different elements has been studied. Recently, the effect of rare earth elements on a-Al grain size and Si morphology, which play a fundamental role in determining the mechanical properties, has attracted attention and studies have focused on this area. Therefore, the effects of the addition of rare earth elements erbium (Er) and europium (Eu) to the A356 alloy at different ratios on the microstructure and mechanical properties of the as-cast and T6 heat-treated condition are investigated in this paper. Grain refinement with the addition of Er and grain coarsening with the addition of Eu were observed. The average grain size decreased by 32% and became 643 μm. On the other hand, the grain size coarsened 36% (873 μm) with the addition of 0.3 Eu to 0.3 Er wt%. The unalloyed as-cast eutectic Si length was 12.0 μm and the Si aspect ratio was 9.6. The acicular long eutectic Si phases had been modified and started to form spherical with T6 state. Although the modification effect on the eutectic Si increases with the increase in the amount of Er, the modification of Eu eutectic Si is much more effective. The most effective eutectic Si modification was achieved by the addition of 0.1 Er + 0.3 Eu wt% with heat treatment when the eutectic Si refined by 80%. The best mechanical properties were obtained with the addition of 0.1 Er with T6 state. In microstructure and fracture surface SEM analysis results, the number and size of intermetallic phases increased with the addition of alloying element. Although these acicular intermetallic phases are reduced in size by heat treatment, they were not fully spherical.

Effect of Mass Fraction of Mischmetal Addition on Microstructures of A356 Alloy

Effect of Cerium-rich Mischmetal on Microstructures of As-cast A356 Alloy

Effect of Mischmetal Modification Treatment on the Microstructure, Tensile Properties, and Fracture Behavior of Al-7.0%Si-0.3%Mg Foundry Aluminum Alloys

Effect of Mixed Rare Earth on A356 Cast Aluminum Alloy at High Die Temperature

Influence of Al-Ti-B Addition on the Microstructure and Mechanical Properties of A356 Alloys

Effects of Mg, Si and Multiple Rare Earth Addition on Microstructures of Al<sub>3</sub>Ti /A356 Composites

Effect of RE on the microstructure and properties of Mg-5Al-Bi alloy

Effects of Mg, Si and multiple rare earth addition on microstructures of Al 3Ti /A356 composites

Microstructure and Mechanical Properties of Mg-3Al-1Zn-xRE Alloys

Effect of Al-Sr-Y intermediate alloy on microstructure and mechanical properties of A356 alloy

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Effects of RE on the Microstructure of Mg-8Zn-4Al Magnesium Alloys

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Effect of Re Addition on Microstructure and Mechanical Properties of Nb-Si-Ti-Al-Cr-Hf Ultrahigh Temperature Alloys

Effects of RE on Microstructures of Mg-8Zn-4Al-0.3Mn Magnesium Alloys

Effect of Re addition on the microstructure and mechanical properties of AlCoCrFeNi 2.1 eutectic high-entropy alloy

The Effect of Mixed RE Elements on Microstructure and Mechanical Properties of Die-Cast AZ91D Alloy

Effects of the addition of Ti powders on the microstructure and mechanical properties of A356 alloy

Effect of Re Addition on the Microstructure and Mechanical Properties of AlCoCrFeNi2.1 Eutectic High-Entropy Alloy

Effect of Rare Earth Elements Erbium and Europium Addition on Microstructure and Mechanical Properties of A356 (Al–7Si–0.3Mg) Alloy

Effect of Al addition on the grain refinement and mechanical properties of as-cast Mg–5Y–4Sm alloys