Abstract:Ultrafine nickel particles have intriguing physical and chemical properties, which are interesting both in fundamental and applied research. The size of the particle was controlled by gas pressure. X-ray diffraction studies showed that fine Ni particles have fcc crystal structure and are coated with thin Ni oxide on the surface. Electron micrographs showed a spherical particle shape, forming a long chain. Size dependence of magnetic properties were studied. The specific magnetic moment drastically decreases when reducing the diameter d of particles <15 nm. The coercivity Hc also approaches zero when d is about 15 nm. Therefore, we can suppose that the critical size for superparamagnetism at room temperature is about 15 nm. According to the superparamagnetic formula KV=25 kT, the value of the magnetic anisotropy constant can be determined, K = −5.8 × 105 (erg/cc). It is found to be larger than bulk Ni [K=−3.4–5.1 × 104 (erg/cc)], the same as Fe particles. The maximum of coercivity at room temperature is about 250 Oe, that is less than the theory value for the coherent rotation model, Hc = 4 K/3Ms=1600 Oe. The mechanism of reversal magnetization can be understood by the sphere chain model. The critical diameter of the single domain is about 65 nm. Curie temperature Tc obviously decreases for 9-nm average diameter particles rather than bulk. It may be in connection with the lattice contraction.

Size control and magnetic properties of single layer monodisperse Ni nanoparticles prepared by magnetron sputtering

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

Size-dependent Magnetic Properties of Branchlike Nickel Oxide Nanocrystals

Preparation and magnetic properties of nickel nanoparticles via the thermal decomposition of nickel organometallic precursor in alkylamines

Size Dependence of the Magnetic Properties of Ni Nanoparticles Prepared by Thermal Decomposition Method

Chemical Synthesis of Monodisperse Fe-Ni Nanoparticles Via A Diffusion-Based Approach

Monodisperse nickel nanoparticles prepared from a monosurfactant system and their magnetic properties

Preparation of hexagonal close-packed nickel nanoparticles via a thermal decomposition approach using nickel acetate tetrahydrate as a precursor

Diameter-Controlled Synthesis of Polycrystalline Nickel Nanowires and Their Size Dependent Magnetic Properties

Improved Magnetic Anisotropy of Monodispersed Triangular Nickel Nanoplates

Magnetic-Properties of Ultrafine Nickel Particles

Fabrication of monodispersed nickel flower-like architectures via a solvent-thermal process and analysis of their magnetic and electromagnetic properties

Fabrication and Characterization of Monodisperse Magnetic Porous Nickel Microspheres As Novel Catalysts

Controlled Synthesis of Magnetic Spinel-Type Nickel Ferrite Nanoparticles by the Interface Reaction and Hydrothermal Crystallization

Size-controlled Synthesis of Nickel Nanoparticles

Size-controlled Synthesis and Magnetic Studies of Monodisperse FePd Nanoparticles.

Size-controlled synthesis of monodisperse superparamagnetic iron oxide nanoparticles

Effects on Direct Synthesis of Large Scale Mono-Disperse Ni0.5zn0.5fe2o4 Nanosized Particles

Synthesis and magnetic properties of nickel nanocrystals

Controlled synthesis of triangular and hexagonal Ni nanosheets and their size-dependent properties

Synthesis of Ni Nanochains with Various Sizes: the Magnetic and Catalytic Properties