Abstract:In this research, tri-block copolymer polycaprolactone-polybutadiene-polycaprolactone (PCL-PB-PCL) (Mn = 2382 g.mol−1) was synthesized via cationic ring-opening polymerization of caprolactone in the presence of hydroxyl-terminated polybutadiene (HTPB) as macroinitiator and different catalysts such as dibutyltin dilaurate, tin (II) 2-ethyl hexanoate, and tetra-n-butyl orthotitanate. This copolymer has a potential application in the propellant industries as a binder. The obtained products were characterized by FT-IR, and 1HNMR spectroscopy gel permeation chromatography (GPC). The thermal behavior of the tri-blockcopolymer was studied by thermogravimetry analysis (TGA) and differential scanning calorimetry (DSC). The result was approved that the glass transition temperature of the tri-block copolymer (Tg = −72.1 °C) is lower than homopolymer PCL (Tg = −65 °C). The effect of heating rate (5,7,10 and 15◦C min−1) on the decomposition of the copolymer was investigated. The kinetic parameter (activation energy for the thermal decomposition of tri-block copolymer) was calculated by the Flynn–Wall–Ozawa (FWO) and Kissinger methods. The polyurethane elastomers were synthesis by the reaction of triblock copolymer and toluene-2,4-diisocyanate diisocyanate(TDI) or isophorone diisocyanate(IPDI) isocyanates with different NCO/OH ratios and in the presence of the plasticizer. The plasticized elastomer with TDI and NCO/OH = 1.2 showed better mechanical properties than IPDI with 0.44 MPa strain and 483% elongation. The average value of the three tensile tests reported as the final result. The effect of 1,4 butanediol as chain extender on mechanical properties of polyurethane-based PCL-PB-PCL was investigated using a tensile test. According to the results, chain extenders caused increasing strength of plasticized elastomer (0.593 MPa) and decreasing its elongation at break (349%).

Synthesis and Characterization of Polyurethane with Carbamic Acid Benzyl Ester Group

Preparation and Properties of Polyurethanes Based on Castor Oil Chemically Modified with Yucca Starch Glycoside

Synthesis and Properties of Polyurethane Ionomers Based on Carboxylated Polycaprolactone

Synthesis and characterization of phosphoryl-choline-capped poly(ε-caprolactone)-poly(ethylene oxide) di-block co-polymers and its surface modification on polyurethanes

Facile Synthesis of Functional Poly( Ε -Caprolactone) Via Janus Polymerization

Synthesis and Characterization of Poly (caprolactone) /Mesoporous Silica Hybrid Materials

Synthesis and properties of polyurethane acrylate oligomer based on polycaprolactone diol

Synthesis and Characterization of Poly(ε‐caprolactone‐co‐δ‐ Valerolactone) with Pendant Carboxylic Functional Groups

Degradability of Poly(epsilon-caprolactone) Bearing Pendant Carboxyl Groups

Effects of flexible and rigid parts of ε-caprolactone and tricyclodecanediol derived polyurethane on the polymer properties of epoxy resin

Epoxy Functionalised Poly(Epsilon-Caprolactone): Synthesis and Application

Novel Poly(ε-Caprolactone)s Bearing Amino Groups: Synthesis, Characterization and Biotinylation

Synthesis and thermal decomposition kinetics of tri-block copolymer ε-caprolactone / polybutadiene (PCL-PB-PCL); preparation of polyurethane network-based tri-block copolymer

Studies on the influence of soft-segment structure on the properties of polyurethane adhesive

Synthesis and Characterization of Graft Copolymers Poly(ethylene Oxide)-G-[poly(ethylene Oxide)-B-poly(ε-caprolactone)] with Double Crystallizable Side Chains

In-Situ Polymerization And Characterization Of Poly (Epsilon -Caprolactone) Urethane/Sio2 Nanocomposites

Effect of Poly(ε-Caprolactone) Glycol Soft Segment Relative Molecular Mass on Properties of Polyurethane Elastomer Based on Poly(ε-Caprolactone) Glycol

Synthesis of novel propylene carbonate diol(PCD)and application in CO2-based polyols waterborne polyurethane

Facile synthesis of polyester-polyether block copolyols for the sustainable high-performance polyurethane reactive hot melt adhesives

Effect of Composition on the Crystallization, Water Absorption, and Biodegradation of Poly(ε-caprolactam -co-ε-caprolactone) Copolymers

Functional poly(carbonate-co-ether) synthesis from glycidyl methacrylate/CO2 copolymerization catalyzed by Zn–Co(III) double metal cyanide complex catalyst