Dielectric and Non-Ohmic Properties of BixNa1 − Xnb2o5.5 + X Ceramics

Zhixiang Li,Gaojie Xu,Yong Li,Aihua Sun,Lei Duan,Jun Jiang,Ping Cui

DOI: https://doi.org/10.1016/j.jallcom.2009.02.148

IF: 6.2

2009-01-01

Journal of Alloys and Compounds

Abstract:A series of BixNa1−xNb2O5.5+x (0.3≤x≤0.7) samples were prepared by solid state reaction method and their structures, electric field–current density (E–J) relationship and dielectric properties were investigated. It was found that the main phase of Bi0.4Na0.6Nb2O5.9 is tungsten bronze structure and the content of tungsten bronze structure phase decreases with increasing Bi content (x). The sample with Bi content (x) around 0.5 shows nonlinear E–J characteristic. Dielectric result shows that Bi0.5Na0.5Nb2O6 is a relaxor type material, and the breakdown field and nonlinear coefficient decrease with increasing temperature. The nonlinear coefficient (α) of 24.8 and dielectric constant of 5.0×105 (1kHz) at 225°C suggest that Bi0.5Na0.5Nb2O6 is a potential candidate for varistor application at high temperature.