Micro-Grinding of Electrochemically Pretreated Ultra-high-Chromium Steel
Chunmei Yang,Lijia Ning,Guannan Jiang,Chenglin Wang,Shuaishuai Wang,Yang Chen,Huanxi Zheng,Jiyu Liu
DOI: https://doi.org/10.1007/s11665-024-10480-z
IF: 2.3
2024-11-28
Journal of Materials Engineering and Performance
Abstract:Ultra-high-strength materials have promising application prospects in various fields, but the high strength may contribute to serious tool wear and poor surface quality. Electrochemical machining (ECM) can effectively alleviate tool wear and improve machinability based on electrochemical dissolution effect. However, it is difficult to control stray electrochemical removal during the ECM process, which may result in "overcut" phenomenon and lower efficiency. In this paper, we propose a new ECM method for machining ultra-high-chromium steel with a hardness of 810 HV. Electrochemical pretreatment is firstly performed; and influences of the electrochemical process on surface microstructure and wettability are investigated. The electrochemical pretreatment generates hierarchical interpenetrating microstructures on the surface, thereby improving machinability. Single-grain scratching and micro-grinding experiments are then performed on untreated and pretreated surfaces. Compared with the untreated surface, grinding forces of pretreated surface are much lower, and bulges caused by plastic flow can be effectively alleviated. Surface roughness Ra of the pretreated surface after grinding is decreased by ~ 42.5%, and wear of diamond grains can be effectively alleviated. The diamond grains have been seriously worn after grinding untreated ultra-high-chromium surface for 1400 mm, and serious material adhesion can be observed. By contrast, no obvious wear is found for the diamond grains after grinding the electrochemically pretreated chromium surface for the same distance. The proposed method can significantly improve machinability of ultra-high-chromium steel and is expected to have promising application prospects in precision machining of difficult-to-cut materials.
materials science, multidisciplinary