Crystal Growth and Luminescent Properties of ZnO Nanowires Prepared by Thermal Vapor Condensation
HU Jun-tao,GUO Chang-xin,CHEN Jian-gang,ZHANG Lin-li
DOI: https://doi.org/10.3321/j.issn:1000-7032.2005.06.018
2005-01-01
Chinese Journal of Luminescence
Abstract:ZnO nanostructures are very promising for applications in field emission displays and photonic devices operating in blue and UV spectral ranges due to its wide band gap(3.37 eV) and large exciton binding energy(60 meV).Therefore,fabrication and properties of ZnO nanostructures have attracted considerable(attention) recently.Various ZnO nanowires have been synthesized by thermal vapor transport and condensation method from the pure Zn powder or a mixture of ZnO,In_2O_3,and graphite powder with a air pressure or a N_2/O_2 pressure.By varying the experimental conditions,we found more ZnO nanostructures such as tetrapods,combs,nanorods and nanobelts.These nanowires have diameters of about 50~1 000 nm,and the length range is about 1~20 μm.The structure of deposited materials was investigated by X-ray diffraction,scanning electron microscopy,transmission electron microscopy and selected area electron diffraction,which reveals the shape of all the ZnO nanowires are hexagonal structure.The luminescent properties of ZnO tetrapods was investigated by excitation spectrum and PL spectrum.The PL spectrum excited with the 210 nm of a Xe lamp at room temperature revealed a strong green emission band centered at about 500 nm with FWHM about 90 nm and a weaker near UV emission band centered at about 380 nm with FWHM about 15 nm.The PL spectrum excited with 325 nm of He-Cd laser at room temperature revealed a strong and narrow near UV emission band centered at about 383 nm with FWHM about 16 nm and a weaker broad emission band centered at(about) 515 nm with FWHM about 76 nm.