Abstract:The growth of high-quality ZnO bulk crystals is an outstanding challenge, and the nature of grown-in defects in crystals is far from well understood. In this work, a specially designed low-temperature-gradient CVT growth system was developed based on finite element analysis. High-quality ZnO single crystals were successfully grown. The supersaturation front in the growth system was controlled, and internal stress in the crystal was reduced by introducing a radiation baffle and a special seed pedestal. The structural, electrical, and optical properties of ZnO crystals were studied before and after oxygen annealing. The scanning electron microscope (SEM) and optical microscope (OM) results indicate the stable growth is achieved under the Zn-rich growth condition. The X-ray rocking curve measurements reveal the high crystalline quality of the grown crystal with the full-width at half-maximum (FWHM) value of 17 arcsec for the (004) reflection. The time-of-flight secondary ion mass spectroscopy (ToF-SIMS) results prove the high purity of grown crystals and reveal the variations of trace impurity concentrations in crystals. When annealed in oxygen at 1000 °C, the optical band gap (Eg) changes from 2.50 eV to 3.15 eV. The Raman analysis indicates that oxygen vacancies (Vo) in the as-grown crystal disappear after annealing. The Hall measurements show that the room temperature (RT) mobilities before and after annealing are 197 cm2V−1c−1 and 207 cm2V−1c−1, respectively. The RT carrier concentration decreases by about two orders of magnitude to 5.45 × 1015 cm−3, while the RT resistivity increases by about one order of magnitude to 5.57 Ω cm after annealing. The positron annihilation lifetimes (PALS) results prove the presence of Zn vacancies (Vzn) after annealing. The origins of as-grown ZnO green luminescence (GL) and the temperature-dependent blue shifts of the GL peak positions are explained based on Zni and Vo defects. The fine structures of annealed ZnO GL are found to be related to Vzn native defects rather than Cu impurity.

Self-organized growth of ZnO single crystal columns array

Vapor phase growth and photoluminescence of oriented-attachment Zn2GeO4 nanorods array

Well-Aligned Zno Nanocolumns Grown by Reactive Electron Beam Evaporation

Solution-based growth and optical properties of self-assembled monocrystalline ZnO ellipsoids.

Growth of ZnO Photonic Crystals by Self-Assembly

On the formation of well-aligned ZnO nanowall networks by catalyst-free thermal evaporation method

STRUCTURAL AND OPTICAL STUDIES OF ZnO FILMS GROWN AT LOW TEMPERATURE

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Structural and Optical Characterizations of ZnO Films Grown by Reactive Electron Beam Evaporation

Crystal growth, finite element analysis and oxygen annealing of ZnO bulk crystal grown by low-temperature-gradient chemical vapor transport

Self-Organized Zno Microcombs With Cuboid Nanobranches By Simple Thermal Evaporation

Surfactant-assisted Self-Assembly Growth of Single-Crystalline ZnO Microflowers at Low Temperature

Growth of aligned ZnO nanorod arrays by catalyst-free pulsed laser deposition methods

Tower-like structure of ZnO nanocolumns

TEM investigations on ZnO nanobelts synthesized via a vapor phase growth

Low-temperature growth and optical properties of radial ZnO nanowires

Growth of ZnO Microrod Array Films and Their Optical Properties

Hierarchical Construction of ZnO Architectures Promoted by Heterogeneous Nucleation

Snowflake-like ZnO structures: Self-assembled growth and characterization

Growth and Formation Mechanism of C-Oriented ZnO Nanorod Arrays Deposited on Glass

Sunlight-assisted Fabrication of a Hierarchical ZnO Nanorod Array Structure