Abstract:The control of the morphology of nanoparticles is a hot issue all over the world.Organic-inorganic materials can be tailor made with an infinite number of architectures and in diverse forms conveniently.A new type of organic inorganic hybrid material was reported to be synthesized by emulsion polymerization by using the monomers which contained alkoxysilane groups.However,polymerization and morphology could hardly be controled during the emulsion process, because the alkoxysilane group was easy to be subjected to hydrolysis and condensation by sol gel process which decreased the stability of the latex.In the present work, organic inorganic hybrid core shell nanoparticles were synthesized by seeded emulsion polymerization.Through morphology design, polystyrene, as seeded cores, was synthesized firstly, then 3 trimethoxysilyl propyl methacrylate (MPS) was added to form MPS styrene copolymer shell on the surface of polystyrene core. Owing to the hydrolysis condensation of organic alkoxysilane groups in MPS,the organic inorganic hybrid shell was formed through sol gel process.The core shell structure was interpreted by thermodynamical representation and characterized by transmission electron microscopy (TEM).The nonionic surfactant used would decrease the stability of the latex.In acidic condition the latex turned into gel just after the addition of MPS,while,in basic condition the particle number decreased obviously, and the latex kept almost stable in neutral condition.The higher the MPS concentration in the emulsion was,the less stability the latex had.Adding MPS continuously could keep the latex more stable and the particle size could be controlled by this method.Then, the core of this kind of hybrid nanoparticles could be dissolved to yield hollow nanocapsules, with the proportion of the void volume 40 1%.

Kinetics and Modeling of Hybrid Core−Shell Nanoparticles Synthesized by Seeded Emulsion (Co)polymerization of Styrene and γ-Methacryloyloxypropyltrimethoxysilane

Kinetics And Modeling Of Hybrid Core-Shell Nanoparticles Synthesized By Seeded Emulsion (Co)Polymerization Of Styrene And Gamma-Methacryloyloxypropyltrimethoxysilane

Synthesis of hybrid core-shell nanoparticles by emulsion (co)polymerization of styrene and gamma-methacryloxy propyl trimethoxy silane : Kinetics and modeling

Synthesis Of Hybrid Core-Shell Nanoparticles By Emulsion (Co)Polymerization Of Styrene And Gamma-Methacryloxypropyltrimethoxysilane

Synthesis of Hybrid Core−Shell Nanoparticles by Emulsion (co)polymerization of Styrene and Γ-Methacryloxypropyltrimethoxysilane

Synthesis of hybrid core-shell nanoparticles by emulsion (Co)polymerization of styrene and γ-methacryloxypropyltrimethoxysilane

Synthesis of organic-inorganic hybrid core-shell nanoparticles and particle size control

Preparation of Hybrid Nanocapsules

EMULSION COPOLYMERIZATION MECHANISM OF 3-TRIMETHOXYSILYLPROPYL METHACRYLATE AND STYRENE

Free radical seeded emulsion polymerization with participation of hydrolysis-condensation reaction ( Ⅱ ) Parameters and modeling application

Synthesis of Hybrid Nanocapsules by Miniemulsion (co)polymerization of Styrene and Γ-Methacryloxypropyltrimethoxysilane

New route to monodispersed amphiphilic core-shell polymer nanoparticles: Polymerization of styrene from α-methylstyrene-containing macroinitiator

Synthesis of Oily Core‐hybrid Shell Nanocapsules Through Interfacial Free Radical Copolymerization in Miniemulsion: Droplet Formation and Nucleation

Preparation of Epoxy‐functionalized Polystyrene/silica Core–shell Composite Nanoparticles

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Melt Rheology of Core-Shell Nanoparticles Filled Polystyrene

Preparation of Functionalized Core‐Shell Alumina/Polystyrene Composite Nanoparticles, 1

Microstructure of the Hybrid Core-Shell Latex Synthesized by Emulsion Copolymerization of 3-Trimethoxysilyl Propyl Methacrylate and Styrene

Modeling of Growth Morphology of Core-Shell Nanoparticles

Synthesis of TiO2–SiO2/polymer Core–shell Microspheres with a Microphase‐inversion Method

Preparation of functionalizable poly(propylene–styrene)/polyacrylonitrile millimeter‐scale particles with core‐shell morphology