Luminescence Characteristics of (Y, Gd)VO4:Eu3+ under UV-VUV Excitation
Wang Bin,Wang Yu-Hua,Zuo Yin-Yan
DOI: https://doi.org/10.3321/j.issn:1001-4861.2006.05.007
2006-01-01
Chinese journal of inorganic chemistry
Abstract:Series of single-phase Y1-xGdxVO4:Eu3+ (0 <= x <= 1) phosphors were synthesized by solid state reaction and their photo-luminescent properties under UV and VUV excitation were investigated. In emission spectra, the intense pure red emission at about 619 nm was observed both under 254 nm and 147 nm excitation and reached its optimal intensity when the ratio of Y/Gd was 0.4/0.6. The luminescent intensity of Y0.4Gd0.6VO4:Eu3+ was about 65% compared with that of commercial available (Y, Gd)BO3:Eu3+ under 147 nm excitation. The VUV excitation spectrum of Y0.4Gd0.6VO4:Eu3+ monitored at 619 nm mainly consists of four band at the peaks of 158 nm, 204 nm, 247 nm and 300 nm, which are attributed to the host absorption and the charge transfer bands of Y3+. Gd3+, Eu3+ absorption. While (Y, Gd)BO3:Eu3+ has centrosymmetric sites for the Eu3+ ions, the Eu3+ ions in (Y, Gd)VO4:Eu3+ occupies the non-centrosymmetric sites. Thus, the (Y, Gd)VO4:Eu3+ shows better color purity under VUV excitation. Their color coordinates were (0.632, 0.355), (0.672, 0.328), respectively.