Luminescence and Optimization of Red Phosphor Ca_4(La_(1-x-y)Gd_xY_y)_(1-n)O(BO_3)_3∶nEu~(3+)

Yang Hu-cheng,Chengyu Li

2005-01-01

Chinese Journal of Luminescence

Abstract:Red phosphor Ca_4(La_(1-x-y)Gd_xY_y)_(1-n)O(BO_3)_3∶nEu~(3+) (LnCOB∶Eu, Ln= La_(1-x-y)Gd_xY_y) was (synthesized) with the method of solid-state reaction at high temperature. The luminescent properties were investigated from vacuum ultraviolet (VUV, E50 000 cm~(-1), λ200 nm) to visible region. The component with best luminescence intensity was found out and compare with commercial red phosphor. This system shows effective red emission under the excitation of low-pressure mercury lamp. The emission spectra of LnCOB∶Eu~(3+) show the characteristic ~5D_0→~7F_J(J=0, 1, 2, 3, 4) transition of Eu~(3+) ions under the excitation of 254 nm. Monitored the strongest ~5D_0→~7F_2 emission line (610 nm), they all have a broad and strong excitation band which centered at about 246 nm which is ascribed to the charge transfer band (CTB) of Eu~(3+)-O~(2-) and result in that the phosphor can be excitated efficiently by low-pressure mercury lamp. In the VUV range, there is a broad host absorption band located around 184~188 nm in the range from 150~200 nm, which include the (f-d) transition of Eu~(3+). And for Ca_4GdO(BO_3)_3∶Eu~(3+), this broad band is very stronger than that in another two hosts, which should be due to the existence of Gd~(3+) ions and the excitation efficiency can be enhanced (around) 184~188 nm effectively.