Abstract:β-BaB2O4 (β-BBO) thin films were successfully synthesized by the sol-gel method using metallo-organic compounds. A stable BBO precursor solution was prepared from barium metal and boron triethoxide or 2,4,6-triethoxycyclotriboroxane in a mixture solvent of ethanol and 2-ethoxyethanol. As-precipitated powder formed by hydrolysis of the precursor solutions crystallized to γ phase, which was transformed to β phase at higher temperatures. The transformation temperatures of powders from γ to β phase of the ethoxide system and the boroxane system were 600 and 680°C, respectively. The calcination of precursor films in a mixture gas of water and oxygen was found to decrease the crystallization temperature ofβ-BBO films on Pt sheet substrates. The precursor films prepared from the ethoxide system and the boroxane system crystallized to β-BBO on Pt (111)/glass substrates at 500 and 550°C, respectively. The BBO films on Pt(111)/glass substrates showed the strong (006) preferred orientation. Theβ-BBO films on Pt(111)/glass substrates showed the second harmonic generation (SHG) of the 532 nm light on irradiation with 1064 nm light. The SH power from the BBO films was correlated with the fundamental power through the square-law proportionality based on the theory. The SHG efficiency of the BBO films was dependent upon the film thickness.

Synthesis of Ba2NaNb5O15 Powders and Thin Films Using Metal Alkoxides

Synthesis of Oriented Ba2NaNb5O15 (BNN) Thin Films from an Alkoxy‐derived Precursor

Synthesis of Lead Barium Niobate Powders and Thin Films by the Sol‐Gel Method

Synthesis of Strontium Barium Niobate Thin Films Through Metal Alkoxide

ChemInform Abstract: Synthesis of Oriented Ba2NaNb5O15 (BNN) Thin Films from an Alkoxy‐Derived Precursor.

Processing of β-BaB2O4 powders and thin films through metal alkoxide

Synthesis and Properties of Highly Oriented (sr, Ba)(Nb, Ta)(2)O-6 Thin Films by Chemical Solution Deposition

Chemical Solution Processing and Characterization of Highly Oriented (ba,ln)nb2o6[ln: La, Gd, Dy] Thin Films

Preparation Of Tungsten Bronze (Sr0.5ba0.5)Nb2o6 Thin Films Using A K0.4(Sr0.75ba0.25)0.8nb2o6 Seed Layer

Properties of Highly Oriented Rare-Earth-Ion-Substituted BaNb2O6Thin Films Synthesized by Chemical Solution Deposition

Chemical Processing of Potassium‐Substituted Strontium Barium Niobate Thin Films Through Metallo‐organics

Properties of highly oriented K(Sr,Ba)2Nb5O15 thin films derived from a metal-alkoxide precursor solution

Preparation and Properties of K(Sr0.75Ba0.25)2Nb5O15 Thin Films by Chemical Solution Deposition Method

Synthesis of Highly Oriented Tungsten Bronze K(Pb0.6ba0.4)(2)Nb5o15 Thin Films by the Chemical Solution Deposition Method

Preparation of Strontium Barium Niobate by Sol-Gel Method

Chemical Processing of Potassium Substituted (Pb0.6Ba0.4)Nb2O6 Powders and Thin Films Through Metallo-Organics

Processing of Β-Bab2o4 Thin Films Through Metal Organics

The Preparation of Strontium Barium Niobate Powders and Films by the Polymeric Precursor Method

Preparation Of Beta-Bab2o4 Powders And Thin-Films By Sol-Gel Method

LOW-TEMPERATURE PREPARATION OF NANO-CRYSTALLINE LITHIUM NIOBATE POWDERS BY THE POLYMERIC PRECURSOR METHOD

Electrochemical Synthesis of Nb-Doped BaTiO3 Nanoparticles with Titanium-Niobium Alloy as Electrode