Abstract:The uncoated γ‐Ce2S3 is easy to decompose and release toxic gas H2S in a humid or acidic environment, and its air thermal stability is limited to 350°C. In this work, we have used heterogeneous precipitation method to coat the surface of γ‐Ce2S3 powder with ZnO nano‐layer, and then used microemulsion method to coat the surface of γ‐Ce2S3@ZnO with SiO2, and successfully prepared γ‐Ce2S3@ZnO@SiO2 composite coating powder. On the premise of not affecting the color rendering performance as much as possible, the thermal stability of γ‐Ce2S3 powder is improved from 350 to 514°C, the time stability is improved from less than 40 days to more than 360 days, and the acid corrosion stability and safety performance are significantly improved. As an environment‐friendly powder with good coloring performance, rare earth sulfide is one kind of the important choices to replace cadmium and lead colorants. In particular, γ‐Ce2S3 belongs to rare earth sesquisulfide, which has a bright red color. However, the uncoated γ‐Ce2S3 is easy to decompose and release H2S in a humid or acidic environment, and its air thermal stability is limited to 350°C. In this work, γ‐Ce2S3 powders coated with zinc oxide were prepared by heterogeneous precipitation method, and a dense protective layer was formed by ZnO to improve chemical and thermal stability. Moreover, silicon dioxide was deposited on the surface of the zinc oxide coating using the microemulsion process to strengthen the powder's acid resistance. The double shells structure greatly promoted thermal stability and acid resistance of γ‐Ce2S3 powders. The results showed that rare earth sulfide powders with double shells have good stability for coloring applications.

Hydrothermal Synthesis of Cadmium Sulfoselenide Inclusion Pigment

Preparation of submicron CdSxSe1-x@ZrSiO4 inclusion pigment and its application in ink-jet printing

Cadmium sulfide nanocrystals via two-step hydrothermal process in microemulsions: synthesis and characterization.

Dual-enhancement of chromaticity and thermal stability: In-situ synthesis of core–shell γ-Ce2S3@CePO4 configuration

Solvothermal Synthesis of Copper Indium Gallium Selenide Powder

Hydrothermal synthesis and characterization of CuIn2.0Se3.5 nanocrystallites

Synthesis and Characterization of CIGS Powder

Noninjection Synthesis of CdS and Alloyed CdS x Se 1−x Nanocrystals Without Nucleation Initiators

In situ hydrothermal synthesis of semiconductor CdS and CdSe nanocrystals by using mesostructured SiO2/CdO composites as precursor

Synthesis of In<sub>2</sub>Se<sub>3</sub>/CuSe Composite Powder by Solvothermal Method

In Situ Hydrothermal Preparation of CdS/polymer Composite Particles with Cadmium-Containing Polymer Latexes

Microemulsion-Mediated Synthesis of Cadmium Zinc Sulfide Nanocrystals with Composition-Modulated Optical Properties

Solvothermal synthesis of nanocrystalline cadmium sulfide

Thermodynamics of arsenates, selenites and sulfates in the oxidation zone of sulfide ores: XII. Mineral equilibria in the Cd–Se–H2O system at 25°C

Facile synthesis of red- to near-infrared-emitting CdTexSe 1-x alloyed quantum dots via a noninjection one-pot route

A hydrothermal method to prepare the spherical ZnS and flower-like CdS microcrystallites

Promoting thermal stability and acid resistance of rare earth sulfide powders by coating ZnO and SiO2 double shells

Zn-doped CdSSe composite quantum dots synthesized by a two-step hydrothermal ion exchange in sensitized solar cells

Luminescence studies of CdS spherical particles via hydrothermal synthesis

Hydrothermal synthesis of PbSe, PbTe semiconductor nanocrystals

Wet Synthesis and Characterization of Mse (M = Cd, Hg) Nanocrystallites at Room Temperature