Effect of low-dose Xe20+ ion irradiation on the deformation behavior of the magnetron sputtered Cr coatings under nanoindentation
Renda Wang,Bingsheng Li,Peng Li,Xue Bai,Lijuan Hu,Qing Huang,Jian Xu,Feng Huang,Fangfang Ge
DOI: https://doi.org/10.1016/j.surfcoat.2021.127907
IF: 4.865
2021-12-01
Surface and Coatings Technology
Abstract:The magnetron sputtered Cr coatings on zirconium (Zr) alloy substrates were irradiated by the 5 MeV Xe20+ ions at room temperature, followed by the studies on microstructure, mechanical properties, and deformation behavior. The coatings exhibit structural integrity without blistering or flaking effects after the 1 × 1014 ions/cm2 irradiation, but the irradiation caused the surface particle refining and the hardening effect. The hardness of the irradiated coating increased ~60% and the indentation modulus decreased ~10%. Moreover, the microstructural characterization was conducted on the tetrahedron indentations by using scanning electron microscope (SEM), atomic force microscope (AFM), and transmission electron microscope (TEM). A piling-up of matter was observed in the indentation of the as-deposited coating, whereas some micro-cracks appeared near the indentation zones on the irradiated coatings. The cross-sectional TEM micrograph of an indentation further revealed the disordering of lattices and the bending of columns in the irradiated area, maybe for the irradiation made the column interface strong so that the column sliding hardly occurred.
physics, applied,materials science, coatings & films