Abstract:Clay minerals are inexpensive, sustainable, and abundant natural minerals being considered as replacements for cement binders. For this purpose, clays have to be activated to improve their pozzolanic activity, i.e., to yield an amorphous aluminosilicate phase that can easily react with calcium hydroxide to form binding phases; additional calcium aluminosilicate hydrate and calcium aluminate hydrates. Activation plays a key role in boosting the cement replacing potential of clay minerals, with the key to understanding activation lying in the control of dehydroxylation. This work promotes mechanochemical activations for comprehensive executing, monitoring and understanding of the dehydroxylation during clay activation. We monitored the mechanochemical conditions, yield degree of amorphization and heat of hydration. Considering the lower dissipation of thermal energy and better control of amorphization mechanochemical conditions were set at 400 rpm for 2 h. Results point out to the disruption of the kaolinite structure on behalf of chemically bound water release and reorganization of Al chemical bonds. The results indicate that with an increase in TGA steps, there are shifts in kaolin dehydroxylation processes, such as water evaporation and spinel crystallization (DTA), as well as shifts in the respective IR bands. Additionally, there is an increase in specific surface area (BET) and a decrease in particle size (SEM, XRD). Calorimetry of the cement paste CEM I 52.5 N indicates an apparently higher thermal reactivity of the aluminate phase compared to the silicate phase as a function of the particle size distribution. The presence of the mechanochemically activated clay changed the morphology, particle size, specific surface area, amorphous content, and thus the availability of pozzolanic aluminum for cement hydration reactions, which is thereby accelerated. It was observed the aluminate phase exhibits higher reactivity. The hydration mechanisms of the silicate (C 3 S) and aluminate (C 3 A) phases as well as the depletion of SO 4 2– ions were affected. Consequently, mechanochemical processing can be utilized as a powerful tool to activate pozzolanic clay with cement-replacing potential.

Activating Process of Geopolymer Source Material: Kaolinite

Geopolymerization of halloysite via alkali-activation: Dependence of microstructures on precalcination

Early-Stage Geopolymerization Process of Metakaolin-Based Geopolymer

MECHANISM OF PHYSICOCHEMICAL CHANGE OF CALCINED KAOLINITE FROM MAOMING

Regulation of Reactivity of Calcined Ultrafine Kaolin Products

XRD and TG-DTA Study of New Alkali Activated Materials Based on Fly Ash with Sand and Glass Powder

Calorimetric study of the pozzolanic potential developed by the mechanochemical activation of kaolin clay

Study of Structural Transformation and Chemical Reactivity of Kaolinite-Based High Ash Slime during Calcination

Undehydrated kaolinite as materials for the preparation of geopolymer through phosphoric acid-activation

Kinetics of the reactive sintering of kaolinite-aluminum hydroxide extrudate

Comparing the reactivity of different natural clays under thermal and alkali activation

Alkli-activated Mechanisms of Kaolinite and Hydrothermal Synthesis of 4A Zeolite

Effects of Activator Types on Degradation Mechanisms of Metakaolin Geopolymer Mortars Exposed to High Temperature

Mechanical and Thermal Properties of Phosphoric Acid Activated Geopolymer Materials Reinforced with Mullite Fibers

Thermal Activation of High-Alumina Coal Gangue Auxiliary Cementitious Admixture: Thermal Transformation, Calcining Product Formation and Mechanical Properties

Effect of Na + alkaline activation on the geopolymerization of a pure metakaolin at room temperature

Mechanical Properties and Reaction Kinetics of Alkali-Activated Metakaolin

Experiment on Activating CaO by Steam in a Rotary Kiln

Thermal stability and microstructure of metakaolin-based geopolymer blended with rice husk ash

Parametrization of Geopolymer Compressive Strength Obtained from Metakaolin Properties

Mineralogical characteristics influence the structure and pozzolanic reactivity of thermally and mechano-chemically activated meta-kaolinites