Abstract:The introduction of Mo and Se vacancies both on the surface and inside of MoSe2 nanosheets is acheived using He+ irradiation to activate the inert basal plane. The high‐density active sites significantly reduce the overpotential of MoSe2 and greatly enhance the hydrogen evolution reaction stability at industry‐level large current density. Developing highly efficient, low cost, and stable electrocatalysts that work at a large current density is crucial for upgrading the current industrial electrochemical water splitting to produce H2. Molybdenum selenide (MoSe2) is a promising 2D transition metal dichalcogenide (TMD), however, its reported output is inadequate due to its inert basal plane. Herein, the catalytic activity of MoSe2 nanosheet arrays is activated by a novel and controllable method of He+ ion irradiation to introduce multiple vacancies simultaneously into their inert basal planes. The vacancies activated MoSe2 have improved electrocatalytic performance and stability with a minimum overpotential of 90 mV at 10 mA cm−2, a Tafel slope of 49 mV dec−1 and high stability of 650 h at the industry‐level large current density of 1000 mA cm−2 compared to several hours for the pristine sample. The DFT results reveal that single Se and single Mo vacancies on the MoSe2 basal plane can efficiently increase the electrical conductivity and reduce energy barriers for water dissociation and subsequent proton adsorption, thus improving the electrocatalytic capability. This finding proves the application of ion beam in defect engineering for effective hydrogen evolution in TMDs‐based catalysts.

Dopant-vacancy activated tetragonal transition metal selenide for hydrogen evolution electrocatalysis

Enriched Se vacancies engineering of RuSe2 induced by low-valence Cu doping for promoting hydrogen evolution and coupling power generation

Coral-like S-doped CoSe2 with Enriched 1T-Phase As Efficient Electrocatalyst for Hydrogen Evolution Reaction

Exploration of Transition Metal Atom-Doped NiSe2 Electrocatalysts for Efficient Alkaline Hydrogen Precipitation Using First Principles Screening

2D/2D Heterojunction of Cobalt‐Iron Selenide Nanolamellas/MXene for Enhanced Electrocatalytic Hydrogen Evolution

Defect Induced Electrocatalytic Hydrogen Properties of Pentagonal PdX2 (X = S, Se)

Dipole Polarization-Driven Spatial Charge Separation in Defective Zinc Cadmium Sulfoselenide for Boosting Photocatalytic Hydrogen Evolution

Heterogeneous Spin States In Ultrathin Nanosheets Induce Subtle Lattice Distortion To Trigger Efficient Hydrogen Evolution

Al-doping-induced electronic structure modulation of CoSe 2 for efficient hydrogen evolution reaction

Stabilizing Pt Single Atoms through Pt-Se Electron Bridges on Vacancy-enriched Nickel Selenide for Efficient Electrocatalytic Hydrogen Evolution.

Nanostructured Ni2SeS on Porous-Carbon Skeletons As Highly Efficient Electrocatalyst for Hydrogen Evolution in Acidic Medium.

Ternary Porous Cobalt Phosphoselenide Nanosheets: an Efficient Electrocatalyst for Electrocatalytic and Photoelectrochemical Water Splitting.

S Dopant-Mediated Hydrogen Evolution Reaction Activity of CoSe2

Constructing 2D PtSe2/PtCo Heterojunctions by Partial Selenization for Enhanced Hydrogen Evolution

Exploration of transition metal atom-doped NiSe 2 electrocatalysts for efficient alkaline hydrogen precipitation using first principles screening

Strategies to enhance the electrocatalytic behavior of metal selenides for hydrogen evolution reaction: A review

Ptse2/Pt Heterointerface With Reduced Coordination For Boosted Hydrogen Evolution Reaction

Trimetallic Zn–Co–Ni Selenide Nanoparticles as Electrocatalysts for the Hydrogen Evolution Reaction

Ion Irradiation Activated Catalytic Activity of MoSe2 Nanosheet for High‐Efficiency Hydrogen Evolution Reaction

Sulfur‐Doped Rhenium Selenide Vertical Nanosheets: A High‐Performance Electrocatalyst for Hydrogen Evolution

Dopant triggered atomic configuration activates water splitting to hydrogen