Preparation of DyVO4 by Sol-Gel Method and Research of Its Photocatalytic Activity
Wenting Tu,Peisong Tang,Xinyu Mu,Wei Yong,Qiuxuan Li,Rong Chen
DOI: https://doi.org/10.1080/10584587.2024.2325870
2024-10-29
Integrated Ferroelectrics
Abstract:Using dysprosium oxide (Dy 2 O 3 ), ammonium metavanadate (NH 4 VO 3 ), nitric acid (HNO 3 ) and citric acid (C 6 H 8 O 7 ·H 2 O) as main raw materials, DyVO 4 was successfully prepared by sol-gel method. DyVO 4 samples were characterized by thermogravimetry differential scanning calorimetry (TG-DSC), X-ray diffraction (XRD), scanning electron microscope (SEM), diffuse reflectance spectrum (DRS) and Fourier transform infrared spectroscopy (FT-IR). Under condition of ultraviolet light, taking 10 mg/L methyl orange solution as simulated sewage, the effects of synthesis temperature and illumination time on the photocatalytic activity of DyVO 4 were studied. The results show that pure tetragonal zircon DyVO 4 samples can be obtained under calcination conditions of 600 °C to 900 °C. The average grain size is about 2 μm and the breadth of band gap is about 3.52 eV. The sample prepared at 800 °C has the best photocatalytic activity. Under ultraviolet light illumination for 150 min, the degradation rate of 10 mg/L methyl orange can reach nearly 100% in presence DyVO 4 . DyVO 4 prepared by sol-gel method is a photocatalyst which has broad application prospect.
engineering, electrical & electronic,physics, condensed matter, applied