The Mechanical Properties of Microscale Area in CNT-C<sub>f</sub>/SiC Hierarchical Composite
Haijun Zhou,Shuhong Dong,Le Gao,Z. Wang,X. F. Zhang,Ping He,Jianbao Hu,Yanmei Kan
DOI: https://doi.org/10.1360/n972014-00468
2015-01-01
Abstract:Carbon nanotubes (CNT) were grown on a carbon fiber surface via a chemical vapor deposition method, and a CNT reinforced Cf/SiC composite was fabricated via a polymer impregnation and pyrolysis process. In this work, we studied the mechanical properties of microscale areas, such as fiber-matrix interfaces modified by CNT, CNT reinforced matrices, and fiber-CNT-matrices in CNT reinforced Cf/SiC hybrid composites. A combination of Vickers indentation and nanoindentation techniques was adopted to elucidate the relationship between the microscopic and macroscopic mechanical properties of the composites. Nanoindentation was used to test the interfacial bonding strength between the fiber and matrix and the hardness of matrices with embedded CNTs. Vickers indentation was used to study the failure behavior of fiber-CNT-matrix units. Interfacial bonding strength was found to be obviously improved by the presence of in situ grown CNTs. Interfacial debonding occurred at the fiber/pyrolytic carbon interphase but not the pyrolytic carbon/CNT interface, indicating that the interface where CNTs were grown possessed a higher bonding strength. Unfortunately, the nanohardness and modulus of the CNT reinforced matrix (Hv=7.5±1.2 GPa, E=62±5.0 GPa) was lower than that of the matrix without CNT (Hv=11.4±0.3 GPa, E=88.0±1.8 GPa). High resolution transmission electron microscope (TEM) images of the CNT/matrix interface showed that the graphitic structure of the CNT wall was likely damaged. This damage of the CNTs and the resulting reduced matrix properties were thought to be caused by serious chemical reaction between CNTs and the Si-C-O amorphous matrix. Vickers indentation measurements were used to determine the combined properties of fiber-CNT-matrix unit. Because whole Vickers indentations were not as clear as those for the pure ceramic, the exact Vickers hardness was not obtained. The indentation size was used to evaluate the damage resistance of the fiber-CNT-matrix unit. Surprisingly, the indentations in the composite with CNTs were smaller than those in composite without CNTs, indicating that the damage resistance of the whole fiber bundle was improved by CNT addition. Thus, the improved fiber/matrix interfacial bonding strength offset the negative effect of the decreased matrix properties. In addition, the damaged CNT-reinforced matrix remained integrated, while the matrix without CNTs showed a crushed morphology. The cracks were bridged by CNTs, and pull-out of CNTs in the cracks were considered responsible for the improved damage tolerance. The increases in debonding toughness and pull-out toughness caused by the CNTs were theoretically calculated. The simulation indicated that the toughening effect of the CNTs may be further improved if the CNT/matrix interface is suitably tailored and the CNTs are well protected.