Abstract:Reusing phosphogypsum (PG) waste to manufacture eco-cementitious materials is sustainable. However, PG faces the challenge of high stacking volume and low utilization rate, and the low-content PG in eco-cementitious materials currently limits its large-scale potential application. This study provides a solution to use high-content PG to fabricate eco-friendly solid waste-based cementitious material (PBC), associated with ground granulated blast furnace slag (GGBS), fly ash (FA), and hydrated lime. Respond surface methodology (RSM) was undertaken to optimize and discuss the influence of independent design factors of GGBS, FA, and hydrated lime content on the unconfined compressive strength (UCS). Besides, the micro-mechanisms and environmental properties of PBC were also investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), and the leachate test. The results indicated that the optimal raw material contents were (by mass): 50.57% PG, 28% GGBS, 20% FA, and 1.43% hydrated lime. The UCS of the optimal PBC mixture is 23.57 MPa at 28 days, which was confirmed via experimental verification (24.65 MPa). Hence, the RSM is an effective method for optimizing PBC's UCS. The micro-mechanisms analysis shows that the ettringite is the primary hydration product within the reaction system of PBC, which is attributed to the substantial amount of PG. The leachate test results indicate that the fluoride ion concentration of the leaching solution of PBC remains below the PG, and the pH value falls within the range of 6–9. The leaching test results meet the Chinese environmental standard of GB 8978-1996. The cost and CO 2 emission of the optimal PBC mixture could achieve a reduction of 71.25% and 99.98%, respectively, compared to Ordinary Portland cement (OPC). The findings of this study could serve as a theoretical foundation for the practical implementation of large-scale and efficient utilization of PG waste. The developed eco-friendly PBC has excellent potential to partially substitute conventional OPC binders and reduce engineering project costs.

Developing high performance phosphogypsum-based cementitious materials for oil-well cementing through a step-by-step optimization method

Development and optimization of phosphogypsum-based geopolymer cement

Eco-friendly solid waste-based cementitious material containing a large amount of phosphogypsum: Performance optimization, micro-mechanisms, and environmental properties

Study on the Mechanical Properties, Microstructure and Hydration Mechanism of Phosphogypsum-Based Geopolymer Cement with Added Micron-Sized Silica Particles

Enhancing Compressive Strength of Phosphogypsum-Based Geopolymer Cement with Five Alkaline Activator Combinations

In-situ remediation of phosphogypsum in a cement-free pathway: Utilization of ground granulated blast furnace slag and NaOH pretreatment

Evaluation of Thermal and Mechanical Properties of Foamed Phosphogypsum-Based Cementitious Materials for Well Cementing in Hydrate Reservoirs

Utilization of untreated-phosphogypsum as filling and binding material in preparing grouting materials

Potential use of phosphogypsum in concrete

Optimization of synergy between cement, slag, and phosphogypsum for marine soft clay solidification

Investigation on the preparation of low carbon cement materials from industrial solid waste phosphogypsum: Clinker preparation, cement properties, and hydration mechanism

An Eco-Friendly Phosphogypsum-Based Cementitious Material: Performance Optimization and Enhancing Mechanisms

A Novel Gypsum-Based Self-Leveling Mortar Produced by Phosphorus Building Gypsum

Hydration process and fluoride solidification mechanism of multi-source solid waste-based phosphogypsum cemented paste backfill under CaO modification

Research on formulation optimization and hydration mechanism of phosphogypsum-based filling cementitious materials

Mechanical properties and soluble phosphorus solidification mechanism of a novel high amount phosphogypsum-based mortar

Utilization of solidified phosphogypsum as Portland cement retarder

The effects of admixtures on the durability properties of phosphogypsum-based cementitious materials

Improving the mechanical property and water resistance of β-hemihydrate phosphogypsum by incorporating ground blast-furnace slag and steel slag

Preparation of phosphogypsum-copper smelting slag-based consolidating body with high compressive strength

Utilization of original phosphogypsum for the preparation of foam concrete