Abstract:In this paper, sulfated ZrO2 were synthesized via precipitation and impregnation method, and the promoting effects of support sulfation on selective catalytic reduction (SCR) performance of CeO2/ZrO2 catalysts were investigated. The results revealed that sulfated ZrO2 could significantly enhance the SCR activity of CeO2/ZrO2 catalysts in a wide temperature range. Especially when S/Zr molar ratio was 0.1, CeO2/ZrO2-0.1S catalyst exhibited a large operating temperature window of 251 ∼ 500 °C and its N2 selectivity was 100 % in the temperature range of 150 ∼ 500 °C. Moreover, CeO2/ZrO2-0.1S catalyst possessed a superior low-temperature activity over 0.1S-CeO2/ZrO2 catalyst. After exposing to 100 ppm SO2 for 15 h, a high NO conversion efficiency of CeO2/ZrO2-0.1S catalyst (90.7 %) could still be reached. The characterization results indicated that ZrO2 treated with a proper dosage of sulfate acid was beneficial to enlarge the specific surface area greatly. Sulfated ZrO2 was also in favor of promoting the transformation of CeO2 from crystalline state to highly-dispersed amorphous state, and inhibiting the transformation of ZrO2 from tetragonal to monoclinic phase. It could also enhance the total surface acidity greatly with an increase in both Brønsted acid sites and Lewis acid sites, thus significantly improving NH3 adsorption on catalyst surface. Besides, the promoting effect of support sulfation on SCR performance of CeO2/ZrO2 catalysts was also related with the enhanced redox property, higher Ce3+/(Ce3++Ce4+) ratio and abundant surface chemisorbed labile oxygen. The in-situ DRIFTS results implied that nitrate species coordinated on the surface of CeO2/ZrO2-0.1S catalyst could participate in the Selective catalytic reduction with ammonia (NH3-SCR) reactions at either medium or high temperature, suggesting that both Eley-Rideal (E-R) and Langmuir-Hinshelwood (L-H) mechanisms might be followed in SCR reactions.

Insight into the promoting effect of support pretreatment with sulfate acid on selective catalytic reduction performance of CeO2/ZrO2 catalysts

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Acid treatment of ZrO2-supported CeO2 catalysts for NH3-SCR of NO: Influence on surface acidity and reaction mechanism

Promoting Metal Oxides–zeolite Electron Interaction on MnCeOx/HY Catalyst for Boosting Nitrogen Oxides Reduction

High-Performance Strategy and Degradation Mechanism of Cezrvox Catalysts for Nox Reduction

Promotional Effect of Zirconium Doping on the NH3‐SCR Activity of CeO2 and CeO2‐TA Modified by Thiourea: A Comparative Study

Influence of Sulfation on CeO2-ZrO2 Catalysts for NO Reduction with NH3

New Understanding of the Promotional Nature of SO2 on Ce-Based Oxide Catalysts for Selective Catalytic Reduction of NO X with NH3

Ceria Supported on Sulfated Zirconia As A Superacid Catalyst for Selective Catalytic Reduction of No with Nh3

Boosting the Low-Temperature Activity and Sulfur Tolerance of CeZr2Ox Catalysts by Antimony Addition for the Selective Catalytic Reduction of NO with Ammonia.

Shape Dependence and Sulfate Promotion of CeO2 for Selective Catalytic Reduction of NO with NH3

The synergistic promotional effect of W doping and sulfate modification on the NH3-SCR activity of CeO2 catalyst

The Contradictory Impact of Sulfation on a CeO<sub><i>x</i></sub>/TiO<sub>2</sub> NH<sub>3</sub>-SCR Catalyst: A Combined Experimental and DFT Study

Enhanced Performance of Iron-Cerium NO Reduction Catalysts by Sulfuric Acid Treatment: the Synergistic Effect of Surface Acidity and Redox Capacity

The Contradictory Impact of Sulfation on a CeOx/TiO2 NH3-SCR Catalyst: A Combined Experimental and DFT Study

The Contradictory Impact of Sulfation on a CeO x /TiO 2 NH 3 -SCR Catalyst: A Combined Experimental and DFT Study

Enhanced alkali resistance of CeO 2 /SO 4 2 − –ZrO 2 catalyst in selective catalytic reduction of NO x by ammonia

Superior PbO-resistance of CeO2/ZrO2 catalyst promoted by solid superacid SO42−/ZrO2 for selective catalytic reduction of NOx with NH3

Effect of SO 2 introduction into CeO 2 on its surface acidity and redox property for the selective catalytic reduction of NO with NH 3

Effects of Anaerobic SO2 Treatment on Nano-Ceo2 of Different Morphologies for Selective Catalytic Reduction of NOx with NH3

Catalytic performance and mechanistic evaluation of sulfated CeO2 cubes for selective catalytic reduction of NOx with ammonia