Abstract:In this paper, sulfated ZrO2 were synthesized via precipitation and impregnation method, and the promoting effects of support sulfation on selective catalytic reduction (SCR) performance of CeO2/ZrO2 catalysts were investigated. The results revealed that sulfated ZrO2 could significantly enhance the SCR activity of CeO2/ZrO2 catalysts in a wide temperature range. Especially when S/Zr molar ratio was 0.1, CeO2/ZrO2-0.1S catalyst exhibited a large operating temperature window of 251 ∼ 500 °C and its N2 selectivity was 100 % in the temperature range of 150 ∼ 500 °C. Moreover, CeO2/ZrO2-0.1S catalyst possessed a superior low-temperature activity over 0.1S-CeO2/ZrO2 catalyst. After exposing to 100 ppm SO2 for 15 h, a high NO conversion efficiency of CeO2/ZrO2-0.1S catalyst (90.7 %) could still be reached. The characterization results indicated that ZrO2 treated with a proper dosage of sulfate acid was beneficial to enlarge the specific surface area greatly. Sulfated ZrO2 was also in favor of promoting the transformation of CeO2 from crystalline state to highly-dispersed amorphous state, and inhibiting the transformation of ZrO2 from tetragonal to monoclinic phase. It could also enhance the total surface acidity greatly with an increase in both Brønsted acid sites and Lewis acid sites, thus significantly improving NH3 adsorption on catalyst surface. Besides, the promoting effect of support sulfation on SCR performance of CeO2/ZrO2 catalysts was also related with the enhanced redox property, higher Ce3+/(Ce3++Ce4+) ratio and abundant surface chemisorbed labile oxygen. The in-situ DRIFTS results implied that nitrate species coordinated on the surface of CeO2/ZrO2-0.1S catalyst could participate in the Selective catalytic reduction with ammonia (NH3-SCR) reactions at either medium or high temperature, suggesting that both Eley-Rideal (E-R) and Langmuir-Hinshelwood (L-H) mechanisms might be followed in SCR reactions.

Acid treatment of ZrO2-supported CeO2 catalysts for NH3-SCR of NO: Influence on surface acidity and reaction mechanism

Investigation on the redox/acidic features of bimetallic MOF-derived CeMOx catalysts for low-temperature NH3-SCR of NOx

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Insight into the promoting effect of support pretreatment with sulfate acid on selective catalytic reduction performance of CeO2/ZrO2 catalysts

Activating low-temperature NH3-SCR catalyst by breaking the strong interface between acid and redox sites: A case of model Ce2(SO4)3-CeO2 study

Effect of SO 2 introduction into CeO 2 on its surface acidity and redox property for the selective catalytic reduction of NO with NH 3

Ceria Supported on Sulfated Zirconia As A Superacid Catalyst for Selective Catalytic Reduction of No with Nh3

Enhanced Performance of Iron-Cerium NO Reduction Catalysts by Sulfuric Acid Treatment: the Synergistic Effect of Surface Acidity and Redox Capacity

Superior PbO-resistance of CeO2/ZrO2 catalyst promoted by solid superacid SO42−/ZrO2 for selective catalytic reduction of NOx with NH3

NH3 treatment of CeO2 nanorods catalyst for improving NH3-SCR of NO

Enhancement of activity and sulfur resistance of CeO2 supported on TiO2-SiO2 for the selective catalytic reduction of NO by NH3

Mechanism of Selective Catalytic Reduction of NOx with NH3 over CeO2-WO3 Catalysts

Influence of Sulfation on CeO2-ZrO2 Catalysts for NO Reduction with NH3

Sb-Containing Metal Oxide Catalysts for the Selective Catalytic Reduction of NOx with NH3

Effects of Anaerobic SO2 Treatment on Nano-Ceo2 of Different Morphologies for Selective Catalytic Reduction of NOx with NH3

Cerium Oxide-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NO x with NH 3 : A Review

Roles of Lewis and Brønsted Acid Sites in NO Reduction with Ammonia on CeO2-ZrO2-NiO-SO42− Catalyst

Ce-O-P Material Supported CeO2 Catalysts: A Novel Catalyst for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Effect of Lean-Oxygen Treatment on the Adsorption and Activity of Zirconium Phosphate @ Ce0.75Z0.25O2 for NH3-SCR Denox

Revealing the effect of paired redox-acid sites on metal oxide catalysts for efficient NO removal by NH3-SCR

Brønsted Acid Enhanced Hexagonal Cerium Phosphate for the Selective Catalytic Reduction of NO with NH3: in Situ DRIFTS and DFT Investigation.