Unraveling the mechanism of sodium storage in low potential region of hard carbons with different microstructures

Huilan Sun,Qiaoyan Zhang,Yanqiang Ma,Zhaojin Li,Di Zhang,Qujiang Sun,Qiujun Wang,Dan Liu,Bo Wang
DOI: https://doi.org/10.1016/j.ensm.2024.103269
IF: 20.4
2024-03-01
Energy Storage Materials
Abstract:The exploration of sodium storage mechanism is of great significance to the development of high-performance hard carbon materials. However, the complex and diverse structure makes the exploration process pretty difficult. Hence, hard carbons with different microstructures were prepared, and the relationship between different microstructures and sodium storage properties was investigated. The results show that “insertion” and “pore-filling” are both effective mechanisms for sodium storage in low potential region. The “pore-filling” mechanism plays an absolutely dominant role in rich-micropores carbons, and pseudo-graphitic layers are the “transport channel” for Na-ions to enter into internal micropores. The density functional theory (DFT) results further confirmed the stronger binding effect of the micropores structure on Na-ions. NMG (magnesium gluconate-derived hard carbons) with abundant micropores can provide a capacity of 346 mAh g−1 at 50 mA g−1. Besides, the capacity maintains 227.7 mAh g−1 after 1000 cycles at a high current density of 1 A g−1. The excellent performance of the full-cells also reflects the great practical application value of NMG.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology
What problem does this paper attempt to address?
### Problems the Paper Attempts to Solve This paper aims to explore the sodium storage mechanisms in hard carbon materials with different microstructures in the low potential region. Specifically, the researchers prepared hard carbon materials with different microstructures and analyzed the relationship between these microstructures and sodium storage performance through experiments and theoretical calculations. The main objectives of the paper include: 1. **Revealing Sodium Storage Mechanisms**: Investigate that in the low potential region, sodium storage in hard carbon materials mainly occurs through two mechanisms: "insertion" and "pore-filling," with the "pore-filling" mechanism playing a dominant role in hard carbon materials rich in micropores. 2. **Optimizing Material Performance**: Improve the sodium storage capacity and cycling stability of the materials by adjusting the microstructure of hard carbon materials, particularly the structure of pseudo-graphitic layers and internal micropores. 3. **Theoretical Validation**: Use density functional theory (DFT) calculations to further confirm the stronger binding effect of micropore structures on sodium ions, explaining why sodium ions tend to choose the "pore-filling" mechanism for storage. ### Main Findings - **"Pore-Filling" Mechanism**: In hard carbon materials rich in micropores, the "pore-filling" mechanism is the main sodium storage method, while the pseudo-graphitic layers only serve as "transport channels" for sodium ions to enter the internal micropores. - **High Capacity and Stability**: The synthesized NMG (magnesium gluconate-derived hard carbon) can provide a high reversible capacity of 346 mAh g⁻¹ at a current density of 50 mA g⁻¹, and after 1000 cycles at a high current density of 1 A g⁻¹, the capacity remains at 227.7 mAh g⁻¹. - **Theoretical Support**: DFT calculation results show that the binding effect of micropore structures on sodium ions is stronger than that of carbon layers, and sodium ions are more inclined to be stored in internal micropores through the "pore-filling" mechanism. ### Experimental Methods - **Material Preparation**: Hard carbon materials with different microstructures, including NMG, NG, and MG, were prepared using different precursors and carbonization conditions. - **Structural Characterization**: The microstructures of the materials were characterized in detail using techniques such as X-ray diffraction (XRD), Raman spectroscopy, nitrogen adsorption-desorption tests (N2 adsorption-desorption), and small-angle X-ray scattering (SAXS). - **Electrochemical Performance Testing**: The sodium storage performance of the materials was evaluated using cyclic voltammetry (CV), galvanostatic charge-discharge tests (GCD), and electrochemical impedance spectroscopy (EIS). ### Conclusion This study reveals the sodium storage mechanisms in hard carbon materials in the low potential region, particularly the importance of the "pore-filling" mechanism in hard carbon materials rich in micropores. This finding provides important theoretical basis and technical support for the development of high-performance sodium-ion battery anode materials.