Unraveling the effect of carbon morphology evolution in hard carbons on sodium storage performance

Huilan Sun,Qiaoyan Zhang,Fei Yuan,Di Zhang,Zhaojin Li,Qiujun Wang,Huan Wang,Bo Wang

DOI: https://doi.org/10.1039/d3qi01497e

IF: 7.779

2023-09-20

Inorganic Chemistry Frontiers

Abstract:Sodium storage of hard carbons in low voltage region is closely correlated with its internal structure. Reasonable microstructure composition and carbon layers spacing are the key to effectively boosting sodium storage capacity. Herein, chitosan-derived hard carbons (CHCs) were prepared via tuning carbonization temperatures. With the increase of carbonization temperature, the internal structure evolved to be ordered and the carbon atoms were rearranged to form more pseudo-graphitic structure. The pseudo-graphitic domains with suitable carbon layers spacing play a crucial role in sodium storage. Carbon layers can significantly accelerate Na-ions insertion/extraction, thus leading to an increased plateau capacity. While the defects and functional groups are conducive to ions transfer, resulting in a good rate. As a result, the optimized material delivers a high specific capacity of up to 317.4 mAh g-1 at 0.5 A g-1, and excellent cycling stability by keeping 238.9 mAh g-1 at 5 A g-1 after 1000 cycles. This work reasonably reveals the relationship between the microstructural evolution of hard carbons and sodium storage performance, which may provide guidance for practical application.

chemistry, inorganic & nuclear