Abstract:Petroleum-derived single-use plastics have dominated a range of material applications, including packaging and service ware (e.g., water bottles, food containers, and drinking straws). However, despite their short-lived service life, the inherent durability, and stability of these plastics have resulted in significant environmental accumulation and spill, contaminating both aquatic and land ecosystems. Consequently, there is a surging interest in the development of bioplastics as a sustainable alternative to petrochemical derived plastics that align with circular economy principles. Among potential materials, cellulose acetate (CA) showcases impressive mechanical properties, optical characteristics, melt processability, and compostability. However, due to its hygroscopic behavior, inferior barrier properties, and lack of dimensional stability, CA applications in the packaging industry are minimal. In this research, the acetylation of lignin and its use as a functional filler for CA matrix was studied. The impact of varying lignin loadings (up to 30 wt.%) on the tensile, morphological, barrier, and viscoelastic properties of the resulting materials was investigated. A thorough characterization of the compression-molded acetylated lignin-CA films revealed a reduction in water uptake (by 59% over baseline), up to a 41.5% reduction in water vapor permeability, and enhanced tensile properties with melt flowability. In summary, the examined films displayed favorable characteristics for use in food and other packaging applications. Consequently, they serve as low carbon footprint, and eco-friendly substitutes for conventional petrochemical-based packaging materials.

Reprocessable cellulose acetate strengthened with boric acid

Reconfigurable Cellulose Acetate‐based Thermosets Cross‐Linked with Diboronic Acid

Strengthening Cellulose Acetate Via Solution-Reprocessible Dynamic Interaction with Poly(4-Pinacolatoborylstyrene) Cross-Linkers

Dynamic covalent bonds of hemiacetals and acetals enables reprocessability and raw material recyclability of high performance cellulosic thermosetting resins

Catalyst-free readily dual-recyclable acetal-based covalent adaptable cellulose networks

Efficient Separation of Acetylated Cellulose from Eucalyptus and Its Enhancement on the Mechanical Strength of Polylactic Acid.

Reversible Adhesives Based on Acrylate Copolymer Modified by Caffeic Acid Containing Boroxin

Efficient and Sustainable Strategy for Recycling of Carbon Fiber-Reinforced Thermoset Composite Waste at Ambient Pressure

A thermadapt epoxy based on borate ester crosslinking and its carbon fiber composite as rapidly processable prepreg

Preparation of highly flexible cellulose acetate membranes modified by hyperbranched poly(amine ester)-epoxidized soybean oil and evaluation of its filtration properties

Improvement of stability for cellulose polymer by calcium oxide for application to porous materials

Recyclable, self-healable and reshape vitrified poly-dimethylsiloxane composite filled with renewable cellulose nanocrystal

Enhancing the Functionality of Biobased Polyester Coating Resins through Modification with Citric Acid

Preparation of carbodiimide-mediated octadecylamine modified carboxyethyl cellulose microfibrils and their reinforcement of poly(butylene adipate-co-terephthalate)

Effect of acetylation of kraft lignin on the blend compatibility with cellulose acetate and the resulting physicomechanical properties

Cellulose Acetate for Shape Memory Polymer: Natural, Simple, High Performance, and Recyclable

New Functional Polymer Materials via Click Chemistry-Based Modification of Cellulose Acetate

Sustainable Upcycling of Waste Banknotes into High-Performance Cellulose Acetate: Properties, Characterization and Environmental Implications

A Multiple Physical Crosslinked Cellulose-Based Bioplastics with Robust Mechanical and Thermal Stability

On the use of cellulose acetate as a structural material for parts produced by fused filament fabrication

Facile one−step preparation of acetylated cellulose nanocrystals and their reinforcing function in cellulose acetate film with improved interfacial compatibility