Abstract:Uniaxial ratcheting and fatigue failure of tempered 42CrMo steel were observed by the tests under the uniaxial stress-controlled cyclic loading with non-zero mean stress [G.Z. Kang, Y.J. Liu, Mater. Sci. Eng. A 472 (2008) 258–268]. Based on the obtained experimental results, the evolution features of whole-life ratcheting behavior and low-cycle fatigue (LCF) damage of the material were discussed first. Then, in the framework of unified visco-plasticity and continuum damage mechanics, a damage-coupled visco-plastic cyclic constitutive model was proposed to simulate the whole-life ratcheting and predict the fatigue failure life of the material presented in the uniaxial stress cycling with non-zero mean stress. In the proposed model, the damage was divided into two parts, i.e., elastic damage and plastic damage, which were described by the evolution equations with the same form but different constants, since the maximum applied stresses in most of loading cases were lower than the nominal yielding strength of the material. The ratcheting of the material was still described by employing a nonlinear kinematic hardening rule based on the Abdel-Karim–Ohno combined kinematic hardening model [M. Abdel Karim, N. Ohno, Int. J. Plast. 16 (2000) 225–240] but extended by considering the effect of damage. The maximum strain criterion combined with an elastic damage threshold was employed to determine the failure life of the material caused by two different failure modes, i.e., fatigue failure (caused by low-cycle fatigue due to plastic shakedown) and ductile failure (caused by large ratcheting strain). The simulated whole-life ratcheting behavior and predicted failure life of tempered 42CrMo steel are in a fairly good agreement with the experimental ones.

Low cycle fatigue behavior of zirconium–titanium–steel composite plate

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

Research on the Fatigue Crack Growth Behavior of a Zr/Ti/Steel Composite Plate with a Crack Normal to the Interface

Low-cycle Fatigue Behavior and Damage Progression of a Fiber Reinforced Titanium Matrix Composite

Micro-scale mechanism for cyclic deformation behavior in Zirconium under low-cycle-fatigue loading

Analysis of the fatigue life of metal composites with a layer of zirconium alloy

Low Cycle Fatigue Behavior and Deformation Mechanisms of Zirconium and Zircaloy-4

Comparisons of low cycle fatigue response, damage mechanism, and life prediction of MarBN steel under stress and strain-controlled modes

Uniaxial ratcheting and fatigue failure of tempered 42CrMo steel: Damage evolution and damage-coupled visco-plastic constitutive model

Effect of reinforcements on rolling contact fatigue behaviors of titanium matrix composite (TiB+TiC)/Ti–6Al–4V

Studying the Damage Evolution and the Micro-Mechanical Response of X8CrMnNi16-6-6 TRIP Steel Matrix and 10% Zirconia Particle Composite Using a Calibrated Physics and Crystal-Plasticity-Based Numerical Simulation Model

Low cycle fatigue and ratcheting properties of steel 40Cr under stress controlled tests

Strain and Stress Controlled Low Cycle Fatigue Behaviors of TC21 alloy

Life Prediction and Failure Analysis in Laser Powder Bed Fused TiC/Ti6Al4V Titanium Matrix Composite under High Cycle and Very High Cycle Fatigue Conditions

Fatigue Behavior of Cracked High-Strength Steel Plates Strengthened by CFRP Sheets

High-cycle random vibration fatigue behavior of CFRP composite thin plates

Low-cycle fatigue behavior for stainless-clad 304+Q235B bimetallic steel

The Micro-Mechanism of Fatigue Crack Propagation for a Forged Mg–Zn–Y–Zr Alloy in the Gigacycle Fatigue Regime

High cycle and very high cycle fatigue of TC17 titanium alloy: Stress ratio effect and fatigue strength modeling

In‐plane biaxial ratcheting effect and low‐cycle fatigue behavior of CP‐Ti based on DIC method