Degradation Behavior of Biobased Epoxy Resins in Mild Acidic Media

Minjie Shen,Megan L. Robertson

DOI: https://doi.org/10.1021/acssuschemeng.0c07621

2020-12-19

Abstract:The accelerated hydrolytic degradation of biobased epoxy resins, prepared through anhydride curing of epoxidized vanillic acid (EVA, a product of lignin depolymerization) and epoxidized soybean oil (ESO), was investigated in acidic solutions. The biobased epoxy resins exhibited sigmoidal degradation kinetics in acidic solutions, consistent with bulk erosion mechanisms observed in linear polyesters. By contrast, earlier work reported surface erosion behavior of these biobased epoxy resins in basic solution. A solid-state reaction order model with autocatalysis was utilized to predict the mass fraction remaining as a function of exposure time in acidic solution, and the data and model were in good agreement. Mass spectrometry and Fourier transform infrared spectroscopy analyses confirmed the degradation mechanism as cleavage of ester groups in the cross-linked structures. The influences of solvent composition and temperature on degradation kinetics were also explored. These results demonstrate that ester-containing epoxy resins undergo hydrolysis in acidic solutions, providing a route for end-of-life management of thermoset waste.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c07621?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c07621</a>.Degradation solution compositions (Table S1); NMR characterization of epoxidized vanillic acid (Figure S1); calculation of theoretical cross-link density and ester density of epoxy resins (Schemes S1 and S2, Figures S2 and S3); degradation data and solid state kinetic model fitting (Figures S4–S7 and S11 and Table S2); mass spectrometry data obtained from degradation products and analysis (Figures S8–S10); and predictions of solubility parameters of degradation products (Table S3) (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c07621/suppl_file/sc0c07621_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology