Toward Forty Thousand‐Cycle Aqueous Zinc‐Iodine Battery: Simultaneously Inhibiting Polyiodides Shuttle and Stabilizing Zinc Anode through a Suspension Electrolyte

Guanhong Chen,Yuanhong Kang,Huiya Yang,Minghao Zhang,Jin Yang,Zeheng Lv,Qilong Wu,Pengxiang Lin,Yang Yang,Jinbao Zhao
DOI: https://doi.org/10.1002/adfm.202300656
IF: 19
2023-04-24
Advanced Functional Materials
Abstract:Vermiculite nanosheets (VS) electrolyte is designed to restrain the shuttle effect of polyiodides and stabilize Zn anode for high‐performance zine‐iodine batteries. Polyiodides can be effectively anchored on the VS surface owing to exposed silica‐oxygen bonds, which are proved by in situ Ultraviolet‐visible spectra. VS interfacial protective layer can prevent reaction between leaked polyiodides and Zn anode, while serving as Zn2+ accelerator for dendrite‐free deposition. Aqueous zinc‐iodine (Zn‐I2) batteries are promising candidates for grid‐scale energy storage due to their safety and cost‐effectiveness. However, the shuttle effect of polyiodides, Zn corrosion, and accumulation of by‐products restrict their applications. Herein, a simple vermiculite nanosheets (VS) suspension electrolyte is designed for simultaneous confinement of polyiodides and stabilization of Zn anode. It is found that the generation of I5− as dominant intermediate and the precipitation reaction between I5− and alkaline by‐products should cause irreversible iodine species loss. Benefiting from the high binding energy between polyiodides and silica‐oxygen bonds of VS, dissolved polyiodides are effectively anchored on the surface of VS suspended in the bulk electrolyte to suppress the shuttle effect, which is confirmed by in situ Raman, Ultraviolet‐visible characterizations and theoretical calculations. Furthermore, the self‐assembly VS interfacial layer on the surface of Zn anode hinders side reactions induced by polyiodides. Meanwhile, the interlayer and surface excess negative charges of VS tend to be compensated by Zn2+ from diffuse layer, which serves as ion accelerators for transferring Zn2+ at the interface immediately, rendering dendrite‐free Zn plating/stripping behavior. Consequently, the Zn‐I2 battery with VS electrolyte achieves an ultra‐long lifespan of 40000 cycles with a negligible capacity decay at 20 C.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology
What problem does this paper attempt to address?
This paper attempts to solve the main problems faced by aqueous zinc - iodine batteries (Zn - I₂ batteries) in practical applications, specifically including: 1. **Polyiodide shuttle effect**: During the charging and discharging process, polyiodides (such as I₃⁻, I₅⁻, I₇⁻, etc.) are prone to form and permeate through the separator, resulting in the loss of active substances and affecting the cycle stability and capacity retention rate of the battery. 2. **Zinc anode corrosion**: Polyiodides react with metallic zinc, leading to zinc corrosion and the growth of zinc dendrites, which may cause battery short - circuit and failure. 3. **By - product accumulation**: By - products (such as ZnO, Zn(OH)₂, Zn - I clusters) generated by zinc corrosion are difficult to redissolve, further exacerbating the decline in battery performance. To solve these problems simultaneously, the research team designed a suspension electrolyte containing vermiculite nanosheets (VS). This electrolyte improves the performance of the battery through the following mechanisms: - **Inhibiting polyiodide shuttle**: By using the strong binding energy between the silicon - oxygen bonds on the surface of vermiculite nanosheets and polyiodides, polyiodides are effectively adsorbed, thereby inhibiting their diffusion and shuttle in the electrolyte. - **Stabilizing the zinc anode**: Vermiculite nanosheets self - assemble on the surface of the zinc anode to form a protective layer, preventing the direct reaction between polyiodides and zinc metal, reducing zinc corrosion and dendrite growth. The experimental results show that the Zn - I₂ battery using this suspension electrolyte can achieve an ultra - long cycle life of more than 40,000 times at a high current density (20 C), and the capacity attenuation is very small, showing excellent cycle stability and Coulombic efficiency. In summary, this paper successfully solves the polyiodide shuttle effect and zinc anode corrosion problems in aqueous zinc - iodine batteries by designing a simple vermiculite nanosheet suspension electrolyte, significantly improving the cycle stability and service life of the battery.