Abstract:An investigation was conducted on the foaming formula and production technique of polyethylene terephthalate (PET) using orthogonal design analysis and Box–Behnken response surface analysis. PET was combined with polyolefin elastomer (POE) and filled with surface‐treated mica, quartz, and graphene oxide (GO). POE served as a carrier and modifier for the foaming agent, as well as a toughening agent. The addition of fillers can improve the thermal properties of PET foaming material. To do this, the blending process includes using a microsphere foaming agent on an open mill at a low temperature of 50°C for 5–6 min. After this, dicumyl peroxide (DCP) and antioxidant are added for 1 min before the specimens are removed from the open mill and flattened. The next step involves placing the specimens in a plate vulcanizing machine at 265°C and 10 MPa for 10 min to initiate the foaming process. The PET foam obtained has a density of 0.4–0.5 g/cm 3 , a tensile strength of 5–6.8 MPa, an elongation at break of 64–276%, and a tear strength of 5.1–14.5 N/m. Scanning electron microscope (SEM) images reveal that the PET foam contains micron‐sized cells, with measurements ranging from about 107 to 273 μm. The tested samples showed that the PET foam with 50 phr of POE, 7 phr of foaming agent, and 5 phr of mica exhibited relatively good mechanical properties, including tensile strength, elongation at break, and tear strength. The thermogravimetric analysis (TGA) indicated that the thermal properties of PET foam are better than those of pure PET. The modified PET foam has many applications due to its low density and excellent properties. This study introduces a new and uncomplicated method for producing PET foam, which differs from the commonly used extrusion foaming process that involves supercritical carbon dioxide or other media.

Investigation on Foaming Ability of Modified Polyethylene Terephthalate (PET) Composites Prepared Using Compression Molding

In-situ polymerization-modification process and foaming of poly(ethylene terephthalate)

Melt Foamability of Reactive Extrusion‐modified Poly(ethylene Terephthalate) with Pyromellitic Dianhydride Using Supercritical Carbon Dioxide As Blowing Agent

Integrated Process of Supercritical Co2-Assisted Melt Polycondensation Modification and Foaming of Poly(Ethylene Terephthalate)

Preparation of Branched and Crosslinked Poly(ethylene terephthalate)and Its Foaming Behavior

Microcellular PETs with High Expansion Ratio Produced by Supercritical CO2 Molding Compression Foaming Process and Their Mechanical Properties

Extrusion Foaming of Poly(ethylene Terephthalate) with Carbon Dioxide Based on Rheology Analysis

Modification of Poly(ethylene Terephthalate) by Combination of Reactive Extrusion and Followed Solid‐state Polycondensation for Melt Foaming

Carbon particulate and controlled-hydrolysis assisted extrusion foaming of semi-crystalline polyethylene terephthalate for the enhanced thermal insulation property

Improvement of Poly(ethylene Terephthalate) Melt-Foamability by Long-Chain Branching with the Combination of Pyromellitic Dianhydride and Triglycidyl Isocyanurate

Molten-state foaming performance of polyethylene terephthalates with supercritical fluids

Morphology and Compressive Properties of Extruded Polyethylene Terephthalate Foam

Lab Analysis of Melt-Foaming Behaviors of Long-Chain Branched Polyethylene Terephthalate Using Supercritical CO2 as Blowing Agent

Sorption Properties of PET Copolyesters and New Approach for Foaming with Filament Extrusion Additive Manufacturing

The Effect of PET Crystal Morphology on Cell Structure

Tailored Morphologies and Properties of High-Performance Microcellular Poly(phenylene Sulfide)/poly(ether Ether Ketone) (PPS/PEEK) Blends

Good Extrusion Foaming Performance of Long‐chain Branched PET Induced by Its Enhanced Crystallization Property

Enzymatic depolymerization of polyester: Foaming as a pretreatment to increase specific surface area

Surface Modification of PET Fiber with Hybrid Coating and Its Effect on the Properties of PP Composites.

Fabrication of Lightweight Polyphenylene Oxide/High‐Impact Polystyrene Composite Bead Foam Parts via In‐Mold Foaming and Molding Technology

Lightweight and High Impact Toughness PP/PET/POE Composite Foams Fabricated by In Situ Nanofibrillation and Microcellular Injection Molding