A dual-purpose separator employing phosphine oxide with metal hydroxide incorporation onto polyethylene matrix to improve interfacial stability and safety of high nickel concentration lithium-ion batteries

Taehoon Kim

DOI: https://doi.org/10.1016/j.colsurfa.2023.132937

2024-02-01

Abstract:In recent years, there has been considerable interest in high nickel concentration oxide batteries, typically denoted as high-Ni NMC, thanks to the substantial specific capacity ( ≤ 200 mAhg-1) and energy density. Nevertheless, the high-Ni NMC battery often encounters challenges related to interfacial problems and fire concerns stemming from the reduction of nickel (Ni) during electrochemical cycling. Herein, a dual-purpose separator incorporating Mg(OH)2 into dimethoxymethyl phosphine oxide (C3H9O3P) on a polyethylene (PE) matrix is proposed for high-Ni NMC batteries. A noteworthy property of the dual-purpose separator is its ability to form a thin and uniform cathode electrolyte interphase (CEI) with approximately 2 nm, primarily composed of robust LiF, on charge-discharge. As a result, the electrochemical stability is improved, demonstrating a high and stable Coulombic efficiency of ∼99.8% with a reduced impedance from ∼155.8 Ω to ∼60.3 Ω. Also, the capacity degradation decreases from 15% to 0.7% for 100 cycles (at C-rate). Another key property of the dual-purpose separator is the strong thermal stability and flame-retardant performance. During combustion test, any flames that appeared are rapidly extinguished in less than 1.0 s due to the combined flame retardant capability from the water release by heat decomposition of Mg(OH)2 and the radical (e.g. OH∙ and H∙) scavenging process by C3H9O3P. Overall, the dual-purpose separator effectively addresses the interfacial challenges and fire safety associated with high-Ni NMC batteries, concurrently, thanks to the synergetic effects between the constituents.

chemistry, physical