Abstract:Purpose This study compares the fatigue performance and biocompatibility of as-built and chemically etched Ti-6Al-4V alloys in TPMS-gyroid and stochastic structures fabricated via Powder Bed Fusion Laser Beam (PBF-LB). This study aims to understand how complex lattice structures and post-manufacturing treatment, particularly chemical etching, affect the mechanical properties, surface morphology, fatigue resistance and biocompatibility of these metamaterials for biomedical applications. Design/methodology/approach Selective Laser Melting (SLM) technology was used to fabricate TPMS-gyroid and Voronoi stochastic designs with three different relative densities (0.2, 0.3 and 0.4) in Ti-6Al-4V ELI alloy. The as-built samples underwent a chemical etching process to enhance surface quality. Mechanical characterization included static compression and dynamic fatigue testing, complemented by scanning electron microscopy (SEM) for surface and failure analysis. The biocompatibility of the samples was assessed through in-vitro cell viability assays using the Alamar Blue assay and cell proliferation studies. Findings Chemical etching significantly improves the surface morphology, mechanical properties and fatigue resistance of both TPMS-gyroid and stochastic structures. Gyroid structures demonstrated superior mechanical performance and fatigue resistance compared to stochastic structures, with etching providing more pronounced benefits in these aspects. In-vitro biocompatibility tests showed high cytocompatibility for both as-built and etched samples, with etched samples exhibiting notably improved cell viability. The study also highlights the importance of design and post-processing in optimizing the performance of Ti64 components for biomedical applications. Originality/value The comparative analysis between as-built and etched conditions, alongside considering different lattice designs, provides valuable information for developing advanced biomedical implants. The demonstration of enhanced fatigue resistance and biocompatibility through etching adds significant value to the field of additive manufacturing, suggesting new avenues for designing and post-processing implantable devices.

Fatigue performance of beta titanium alloy topological porous structures fabricated by laser powder bed fusion

Investigation of fatigue behavior of laser powder bed fusion Ti-6Al-4V: Roles of heat treatment and microstructure

The effect of microstructure on the fatigue behavior of titanium alloy graded porous structures fabricated by selective laser melting

Understanding the Relations between Surface Stress State and Microstructure Feature for Enhancing the Fatigue Performance of TC6 Titanium Alloy

Fatigue behavior of thin-walled grade 2 titanium samples processed by selective laser melting. Application to life prediction of porous titanium implants

Porous NiTiNb alloys with superior strength and ductility induced by modulating eutectic microregion

Effects of porosity gradient pattern on mechanical performance of additive manufactured Ti-6Al-4V functionally graded porous structure

Fatigue behaviour of titanium scaffolds with hierarchical porosity produced by material extrusion additive manufacturing

Fatigue behaviour of L-DED processed Ti-6Al-4V with microstructures refined by trace boron addition

Compressive properties and deformation mechanism of selective laser melting of Ti6Al4V porous femoral implants based on topological optimization

Microstructure and pore sensitivities in very high cycle fatigue behaviors of titanium alloy welded joints under stress ratios

Strength Properties of a Porous Titanium Alloy Ti6Al4V with Diamond Structure Obtained by Laser Power Bed Fusion (LPBF)

Comparative fatigue performance of as-built vs etched Ti64 in TPMS-gyroid and stochastic structures fabricated via PBF-LB for biomedical applications

Microstructural evolution and oxidation in α/β titanium alloy under fretting fatigue loading

Research Viewpoint on Performance Enhancement for Very-High-Cycle Fatigue of Ti-6Al-4V Alloys via Laser-Based Powder Bed Fusion

Analysis of Room-Temperature/High-temperature High-Cycle Fatigue Performance of Laser Additive Manufactured Ti65 Titanium Alloy

Quasi-static Compression and Compression-Compression Fatigue Behavior of Regular and Irregular Cellular Biomaterials

Effect of processing parameters on the defects, microstructure, and property evaluation of Ti-6Al-4V titanium alloy processed by laser powder bed fusion

Laser Powder Bed Fusion of Metastable Β Titanium Alloys: Enhanced Strength and Plasticity Through Simultaneous Activation of Multiple Deformation Mechanisms

Experimental and numerical study of the compressive fatigue behavior of a Ti6Al4V mapped rhombioidal dodecahedral structure fabricated by electron beam melting

Fatigue and tensile deformation behaviors of laser powder bed fused 304L austenitic stainless steel