Abstract:Based on the response surface methodology (RSM), Cu-Mn-Ce catalysts were prepared via the vacuum impregnation method. Also, Their performance in the oxidation of a tar model compound (Benzene, 5,000 ppm) was evaluated. Results show that the optimum condition is CuO-MnO content of 30% and CeO2 content of 4.4% at a calcination temperature of 620 °C for 4.1 h. In this condition, the confirmatory experiment indicates the average carbon conversion rate within half an hour (Xc-0.5h) and four hours (Xc-4h) are 99.5% and 97.1% at 300 °C, respectively, which is in good agreement with the model prediction. XRD, H2-TPR, SEM, and XPS were employed in catalyst characterization. CuO is the primary active metal in the catalysts, which is affected easily by the calcination temperature. A lower calcination temperature tends to cause a weak structure strength, but a higher temperature results in impairing the reducibility. The major roles of CeO2 are displayed in two aspects that CeO2 increases the dispersion of the active metal, enhances the catalyst stability, and increases the oxygen vacancies and improves the oxygen transfer ability. For Cu-Mn-Ce composite catalyst, the catalytic oxidization of benzene complies with the Mars-van Krevelen mechanism (MVK). The content of CuO-MnO determines the number of active sites on the catalyst, which promotes the reduction of catalyst. CeO2 plays an important role in enhancing the oxidization of the catalyst. Therefore, the ratio of CuO-MnO to CeO2 in the catalyst will cause a change of the control step of the redox reaction.

Performance of Cu-MCM-41 catalyst for catalytic oxidation of 1,2,4-trimethylbenzene

Preparation of Bimetallic CuZn@mSiO2 Yolk‐Shell Catalyst for the Selective Oxidation of Cumene to Acetophenone

Catalytic Performance of Cu-MCM-41 with High Copper Content for the Direct Hydroxylation of Benzene to Phenol

MCM-41 supported Cu-Mn catalysts for catalytic oxidation of toluene at low temperatures.

Mofs-derived CuCeOx Supported on H-zeolite Socony Mobile-5 for Catalytic Oxidation of 1,2-Dichlorobenzene

Improved activity and stability for chlorobenzene oxidation over ternary Cu-Mn-O-Ce solid solution supported on cordierite

Preparation, Characterization and Desulfurization Performance of Cu/Ti-MCM-41 and Cu/Ti-HMS Catalysts

Catalytic oxidation of benzene over alumina-supported Cu-Mn-Ce mixed oxide catalysts

Role of Pore Size and Surface Properties of Ti-MCM-41 Catalysts in the Hydroxylation of Aromatics in the Liquid Phase

Synthesis of 2,3,5-Trimethyl-1,4-Benzoquinone via Catalytic Oxidation of 2,3,6-Trimethylphenol with CuCl2 and FeCl3

Benzaldehyde reduction over Cu-MCM-41 catalyst: Influence of the Si/Cu ratio during hydrothermal synthesis on the structure and catalytic properties

Cu-incorporated Mesoporous Materials: Synthesis, Characterization and Catalytic Activity in Phenol Hydroxylation

Insight into the catalytic performance and reaction routes for toluene total oxidation over facilely prepared Mn-Cu bimetallic oxide catalysts

Synthesis of CuI-modified thiol-functionalized MCM-41 silica-based materials and their catalytic tetralin performance

SYNTHESIS OF TS-1 MONOLITHIC CATALYST AND ITS CATALYTIC PERFORMANCE FOR HYDROXYLATION OF BENZENE

STRUCTURAL CHARACTERISTICS OF Ti-MCM-41 AND THE CHEMISTRY SELECTIVITY IN THE HYDROXYLATION OF BENZENE

Enhanced Catalytic Performance and Poison Resistance of Cu–Mn–Ce Ternary Mixed Oxide for Chlorobenzene Oxidation

Experimental and Kinetic Investigation of 1,2,4-Trimethylbenzene Oxidation at Low Temperature

Preparation of Mesoporous Supported CuCo2O4 Catalyst and Selective Oxidation of Benzyl Alcohol

Promoting Effect of Ti on MnTiOx Catalysts for Benzene Highly Efficient Oxidation

Preparation of MnOx/TiO2 composites and their properties for catalytic oxidation of chlorobenzene.