Abstract:The present investigation was conducted on the low-speed impact response of quasi-isotropic [±45/0/90°]xs hybrid composite through laboratory level experimental tests. The purpose was to understand the behaviour that the different stacking sequences of hybrid glass/carbon fibre composites has on the ability of the material to sustain loads during low-speed impact events without developing critical structural failure in the material and improving the impact energy absorption properties, which is a relevant matter in aerospace and automotive industries. Drop-weight impact tests were carried out on two different laminates, with different stacking sequences, each of which were 16 symmetric inter-ply hybrid laminates named GC [+45G/−45C/0G/90C]4s and, respectively, G-C [+45G/−45G/0G/90G/+45C/−45C/0C/90C]2s, where G stands for glass fibre and C for carbon fibre. Both were comprised of epoxy matrix reinforced carbon/E-glass fibre woven fabric composites. The outcome of changing the hybrid stacking sequence, on the impact performances, was discussed. The damage morphologies and local failure mechanisms were analysed using visual inspection and a high-resolution laser scanner. Under 33 J impact energy, both tested hybrid composites exhibited approximately 10 kN peak load. Nevertheless, one key parameter, the time to peak load, significantly changed; the damage initiation threshold for GC samples occurred immediately before 6 kN, whereas for G-C samples this threshold appeared much earlier. This type of behaviour was partly connected to the delay in the propagation of delamination and fibre breakage, which was influenced by the high elastic energy absorption of the carbon fibres when compared with the glass fibres. The absorbed energy was higher for GC configuration, whereas a higher DI was observed for samples G-C indicating that a high percentage of the total energy was dissipated through the propagation of in-plane and out-of-plane fibre/matrix cracks. No perforation was observed on either configuration; nevertheless, the damage area significantly changed both in size and appearance from one configuration to another.

Impact and Post-Impact Damage Response of Interlayer Nonwoven Reinforced Hybrid Composites

Post-Damage Compressive Strength of Woven Hybrid Composites Impacted with Various Energy Levels

Investigation on Layer Hybridization of Glass/Carbon Fibre Woven Reinforced Composites Subjected to Low-Speed Impact

Low-velocity impact and compression-after-impact behaviors of twill woven carbon fiber/glass fiber hybrid composite laminates with flame retardant epoxy resin

Low-velocity impact response of 3D woven hybrid epoxy composites with carbon and heterocyclic aramid fibres

Flexural and low velocity impact behaviour of hybrid metal wire mesh/carbon-fibre reinforced epoxy laminates

The influence of the inter-ply hybridisation on the mechanical performance of composite laminates: Experimental and numerical analysis

Influence of yarn-hybridisation on the mechanical performance and thermal conductivity of composite laminates

Impact response of hybrid composites under varying environmental conditions: A comparative study

Hybridization effect of Kevlar and glass fiber on carbon/epoxy composites to enhance the damage strength under low velocity impact. Part II: Numerical simulations

Investigations on the development of impact-resistant thermoplastic fibre hybrid composites from glass and steel fibre

Influence of Fibre Architecture on Impact Damage Tolerance in 3D Woven Composites

Mechanical Characterization and Impact Damage Assessment of Hybrid Three-Dimensional Five-Directional Composites

Investigation of shear thickening fluid (STF) impregnated interlayer hybrid composites under low-velocity impact loading

High‐velocity impact behavior of nonwoven mats and unidirectional prepreg hemp and flax fibers reinforced hybrid biocomposites

Experimental study of the importance of fibre breakage on the strength of thermoplastic matrix composites subjected to compression after impact

Low-velocity impact and static behaviors of high-resilience thermal-bonding inter/intra-ply hybrid composites

Enhancing damage resistance in tubular triaxial hybrid braided composites: Innovative production and tensile modulus prediction with damage analysis

Investigation of the energy absorption behavior and damage mechanisms of aramid/carbon/jute fiber hybrid epoxy composites

Experimental and numerical investigations on the dynamic response of woven carbon fiber reinforced thick composite laminates under low-velocity impact

Experimental studies of low-velocity impact behavior on hybrid metal wire net/woven carbon-fiber reinforced composite laminates