Abstract:Deterioration of concrete infrastructures occurs for several reasons, leading to operational problems and further collapse. Freezing-thawing processes are one of the active damage mechanisms in cold regions causing defect accumulation in the inner structure of the material and reduction of the mechanical properties. The optimal way to evaluate the damage degree is by applying non-destructive testing (NDT) methods which allow detailed and integrated results. In this research, a relationship between Acoustic Emission (AE) release energy trend and X-ray Computed Tomography (CT) parameters was investigated for damage quantification. Visualization and extraction of the internal concrete components were conducted by X-ray CT. The ultrasonic pulse velocity (UPV) and resonant frequency methods were employed for the determination of the dynamic modulus of elasticity. After utilizing AE on the compression test, the damage characterization was evaluated. The extensive description of structural members in in-service structure was acquired using principal component analysis (PCA). The X-ray CT results show that all specimens have initial damage degrees in form of cracks and voids unevenly distributed within the concrete matrix. Regarding the irrigation structure, all concrete specimens have unique particle characteristics depending on which structural members they were drilled out from. Moreover, it is observed that the accumulated damage in the form of voids positively correlates with the initial AE energy release rate. In concrete specimens with low damage degrees, the AE energy release has an upward trend of low amplitude (≤50 dB) with a silent stage at the initial loading and sudden release only near the final failure. In contrast, heavily damaged concrete shows continuous AE energy release of high amplitude (≥60 dB) and with a high initial AE energy release rate corresponding to the uninterrupted crack propagation and coalescence in the early stage of fracture and throughout the loading due to the high weak zones ratio. These results indicate that frost damage can be evaluated by the comprehensive analysis of the fracture process of concrete based on X-ray CT and AE results to characterize the damage degree.

Evaluating concrete quality under freeze–thaw damage using the drilling powder method

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

A Gaussian Processes-Based Approach for Damage Detection of Concrete Structure Using Temperature-Induced Strain

Evaluation of freeze-thaw damage on concrete material and prestressed concrete specimens

Structural behaviors evaluation of RC beam under frost damage - A methodology with meso-macro material/bond simulation and integrating into structural analysis

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Study on Freezing-Thawing damage mechanism and evolution model of concrete

Two‐dimensional Rigid Body Spring Method Based Micro‐mesoscale Study of Mechanical Strengthening/damaging Effects to Concrete by Frost Action

The durability of concrete subject to mechanical load coupled with freeze–thaw cycles: a review

Experimental Examination of Electrical Characteristics for Portland Cement Mortar Frost Damage Evaluation

A stochastic damage model for evaluating the internal deterioration of concrete due to freeze–thaw action

Mesoscale Simulation of Fatigue Behavior of Concrete Materials Damaged by Freeze-Thaw Cycles

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles

Experimental Investigation of the Deformational Behavior of the Interfacial Transition Zone (itz) in Concrete During Freezing and Thawing Cycles

Environmental Factors Influencing The Durability Of Concrete Structures In Frost Environments

Frost damage evaluation of concrete irrigation structure by X-ray CT and AE energy release trend at the initial loading stage

Damage evaluation method based on ultrasound technique for gangue concrete under freezing-thawing cycles

Experimental Evaluation of the Concrete Damage and Pore Characteristics under Salt-Freezing Cycles

Freeze–Thaw Damage Characteristics of Concrete Based on Compressive Mechanical Properties and Acoustic Parameters

Assessment and mitigation of early-age cracking for on-site concrete structures by a combined scheme using Temperature Stress Testing Machine (TSTM) and long-span restraining frame

Multi-Scale Analysis of the Damage Evolution of Coal Gangue Coarse Aggregate Concrete after Freeze–Thaw Cycle Based on CT Technology